Abstract: A porous material of a polytetrafluoroethylene (PTFE), which can retain at least 90% of 0.109 .mu.m latex spheres and has a flow rate (IPA flow rate) of at least 0.6 ml/cm.sup.2 /min as measured with isopropyl alcohol under a differential pressure of 1 kg/cm.sup.2. A process for the production of a porous material of PTFE, which comprises, after forming a molded article from fine powder of PTFE by paste extrusion, (1) sintering the molded article, (2) rolling up the molded article thus sintered and heat-treating it at a temperature lower than the melting point of the polytetrafluoroethylene in a state as rolled up, and then (3) stretching the molded article thus heat-treated in at least an uniaxial direction. The porous material of PTFE according to the present invention has micropores and good permeability and particularly is excellent in performance of retaining fine particles.

Abstract: In the connection or terminal portions of cross-linked polyethylene cables produced by winding irradiated tapes around the connection or terminal portions of cross-linked polyethylene insulated cables and heat molding the same, the irradiated tapes comprise polyethylene and/or an ethylene copolymer as a base resin plus an ethylene-vinyl acetate copolymer containing more than about 15% vinylacetate (VA) in an amount which provides more than an about 2.5% VA content in the irradiated tapes.

Abstract: Electric wires or cables having a dielectric layer or layers of an uncross-linked or cross-linked mixture of (1) a polyolefin and (2a) polystyrene or (2b) a styrene copolymer. The polystyrene is present in such an amount as to provide a 10 to 30% styrene content, based on the entire mixture weight, while if the styrene copolymer is used it is present in such an amount as to provide a 3 to 30% styrene content, based on the entire mixture weight. The mixture may comprise, alternatively, both polystyrene and a styrene copolymer in an amount so as to provide a 10 to 30% and a 5 to 20% styrene content, due to the former and the later, respectively, based on the entire mixture weight.