Abstract: A paper feed roller (5) is divided into a first roller (5a) and a second roller (5b); a slit (58) through which about 10 to 20 sheets of documents can pass is formed between the first roller and a gate plate (57) opposite to this; and the paper fed out therefrom is fed out to a space between the second roller (5b) and a separation pad (7) in contact with this.Also, there is adopted a construction in which the pressing force of a paper conveyance spring is transformed by a slide cam sliding in a direction parallel to the paper feed roller; and the paper width detection sensor is assembled by a fitting construction.

Abstract: A paper feed roller (5) is divided into a first roller (5a) and a second roller (5b); a slit (58) through which about 10 to 20 sheets of documents can pass is formed between the first roller and a gate plate (57) opposite to this; and the paper fed out therefrom is fed out to a space between the second roller (5b) and a separation pad (7) in contact with this.Also, there is adopted a construction in which the pressing force of a paper conveyance spring is transformed by a slide cam sliding in a direction parallel to the paper feed roller; and the paper width detection sensor is assembled by a fitting construction.

Abstract: A molding resin composition comprising 99.9 to 50% by weight of polyimide represented by the formula: ##STR1## and 0.1 to 50% by weight of polyether ketone resin and/or polyester resin, and more particularly comprising the polyester resin capable of forming an anisotropical molten phase at a temperature of 420.degree. C. or less, and a polyimide-based molding resin composition which comprises the said resins and other additives such as phenolic resin, fluororesin, graphite, carbon fibers, aromatic polyamide fibers, potassium titanate fibers and a crystallization accelerator, and is excellent in thermal resistance, chemical resistance, mechanical strength and processability.

Abstract: Provided are carbon-fiber-reinforced polyimide resin compositions having excellent mechanical strength. The compositions are formed of (a) 5-50 parts by weight of carbon fibers, which have been obtained by coating starting carbon fibers at surfaces thereof with an aromatic polysulfone resin and then heating the thus-coated carbon fibers at 300.degree.-400.degree. C., and (b) 95-50 parts by weight of a polyimide resin which perferably have recurring units of following formula: ##STR1## wherein X represents a specific divalent radical and R represents a particular tetra-valent radical.

Abstract: A process for the production of polyimide fibers and polyimide fibers obtained by the process. The process includes thermal or chemical imidation of a polyamic acid which has been obtained by reacting a specific diamine and a particular tetracarboxylic dianhydride in the presence of a dicarboxylic anhydride represented by the following formula: ##STR1## wherein Z represents a divalent group selected from the group consisting of monocyclic aromatic groups, fused polycyclic aromatic groups and non-fused polycyclic aromatic groups with aromatic rings bonded together directly or via a crosslinking member.