Abstract: A method for forming a zinc alloy powder for use in an alkaline battery includes: obtaining a zinc molten metal in which zinc is melted; melting a zinc-aluminum master alloy in the zinc molten metal, thereby obtaining an aluminum-contained zinc alloy molten metal; and producing an aluminum-contained zinc alloy powder by powdering the aluminum-contained zinc alloy molten metal.

Abstract: Disclosed is manganese dioxide having a peak intensity ratio between a peak intensity I? in a vicinity of 525 cm?1 and a peak intensity I? in a vicinity of 580 cm?1: I?/I? of 0.62 or less, when measured by Raman scattering spectroscopy. Also disclosed is an alkaline dry battery comprising: a cylindrical positive electrode having a hollow, the positive electrode including the foregoing manganese dioxide; a gelled negative electrode including a negative electrode active material filled in the hollow of the positive electrode; a separator disposed between the positive electrode and the gelled negative electrode; a negative electrode current collector inserted in the gelled negative electrode; a negative terminal plate electrically connected to the negative electrode current collector; and an electrolyte.

Abstract: A method for forming a zinc alloy powder for use in an alkaline battery includes: obtaining a zinc molten metal in which zinc is melted; melting a zinc-aluminum master alloy in the zinc molten metal, thereby obtaining an aluminum-contained zinc alloy molten metal; and producing an aluminum-contained zinc alloy powder by powdering the aluminum-contained zinc alloy molten metal.

Abstract: Disclosed is an alkaline primary battery including: a bottomed cylindrical battery case; a cylindrical positive electrode having a hollow, being in contact with an inner wall of the battery case, and including manganese dioxide; a gel negative electrode being in the hollow of the positive electrode, and including zinc or a zinc alloy; a separator interposed between the positive electrode and the negative electrode; and an alkaline electrolyte. The positive electrode has an electric capacity C1 and a height L1, the negative electrode has an electric capacity C2 and a height L2, the electric capacity C1 and the electric capacity C2 satisfy the relational expression (1): 1.05?C2/C1?1.25 ??(1), and the height L1 and the height L2 satisfy the relational expression (2): 0.85?L2/L1?f(C2/C1) ??(2), where f(C2/C1)=?0.3058×C2/C1+1.3153.