Abstract: A method for preparing modified calcined kaolin particles with surface amphiphilicity. The method includes the steps of drying and sieving the calcined kaolin particles, adding ethanol, and stirring to obtain a suspension A, preparing an ethanol solution of a vinyl silane coupling agent, and stirring for a period of time at a certain temperature to obtain a solution B, dripping the solution B into the solution A, and stirring for a period of time at a certain temperature to obtain a suspension C, reducing the temperature of the suspension C, introducing nitrogen, adding a certain amount of sulfhydryl compound, stirring for a period of time at a certain temperature to obtain a suspension D, filtering, washing and drying to obtain the modified calcined kaolin particles.

Abstract: A method for preparing modified calcined kaolin particles with surface amphiphilicity. The method includes the steps of drying and sieving the calcined kaolin particles, adding ethanol, and stirring to obtain a suspension A, preparing an ethanol solution of a vinyl silane coupling agent, and stirring for a period of time at a certain temperature to obtain a solution B, dripping the solution B into the solution A, and stirring for a period of time at a certain temperature to obtain a suspension C, reducing the temperature of the suspension C, introducing nitrogen, adding a certain amount of sulfhydryl compound, stirring for a period of time at a certain temperature to obtain a suspension D, filtering, washing and drying to obtain the modified calcined kaolin particles.

Abstract: A method for preparing cracking catalyst. The method comprises making catalyst slurry having a homogeneous distribution of molecular sieve slurry, pseudoboehmite, clay, inorganic acid and aluminum-containing binder; and subsequent spray drying. Inorganic acid is added prior to the addition of pseudoboehmite; addition of molecular sieve is added after the addition of inorganic acid; and a phosphatic dispersant is added during preparation. Compared to conventional methods of preparing FCC catalyst slurry, the inventive catalyst slurry viscosity is decreased and the fluidity thereof is improved, while catalyst anti-friction is maintained. The solid content of the FCC catalyst slurry can be increased to about 40% or more. The gel forming time is significantly reduced with increased productivity and decreased catalyst production cost. Meanwhile, the catalyst has high pore volume and improved micro-reactivity. Overall reactivity performance of the catalyst is also improved.

Abstract: A method for preparing cracking catalyst. The method comprises making catalyst slurry having a homogeneous distribution of molecular sieve slurry, pseudoboehmite, clay, inorganic acid and aluminum-containing binder; and subsequent spray drying. Inorganic acid is added prior to the addition of pseudoboehmite; addition of molecular sieve is added after the addition of inorganic acid; and a phosphatic dispersant is added during preparation. Compared to conventional methods of preparing FCC catalyst slurry, the inventive catalyst slurry viscosity is decreased and the fluidity thereof is improved, while catalyst anti-friction is maintained. The solid content of the FCC catalyst slurry can be increased to about 40% or more. The gel forming time is significantly reduced with increased productivity and decreased catalyst production cost. Meanwhile, the catalyst has high pore volume and improved micro-reactivity. Overall reactivity performance of the catalyst is also improved.