Abstract: Provided is a glove which has good adhesiveness to a rubber or resin coating material and excellent durability and further fits a hand well enabling good work efficiency. The glove is knitted from a covered yarn obtained by winding a sheath yarn around a core yarn and at least a part of the surface thereof is coated with a rubber or resin coating material, wherein the sheath yarn is a crimped yarn made of a high strength fiber having, as a property of a raw yarn, a tensile strength of 1.75 N/tex or more as measured according to JIS L 1013 8.5, and the crimped yarn simultaneously satisfies the following (1) to (3): (1) a degree of bulkiness of 40 cm3/g or more as measured according to JIS L 1013 8.16 A method after hot water treatment at 90° C. for 20 minutes, (2) a bulk compression modulus of 80% or more as measured according to the same method, and (3) a shrinkage/elongation ratio of 20% or more as measured according to JIS L 1013 8.11 A method.

Abstract: Provided is a glove which has good adhesiveness to a rubber or resin coating material and excellent durability and further fits a hand well enabling good work efficiency. The glove is knitted from a covered yarn obtained by winding a sheath yarn around a core yarn and at least a part of the surface thereof is coated with a rubber or resin coating material, wherein the sheath yarn is a crimped yarn made of a high strength fiber having, as a property of a raw yarn, a tensile strength of 1.75 N/tex or more as measured according to JIS L 1013 8.5, and the crimped yarn simultaneously satisfies the following (1) to (3): (1) a degree of bulkiness of 40 cm3/g or more as measured according to JIS L 1013 8.16 A method after hot water treatment at 90° C. for 20 minutes, (2) a bulk compression modulus of 80% or more as measured according to the same method, and (3) a shrinkage/elongation ratio of 20% or more as measured according to JIS L 1013 8.11 A method.