Abstract: A hydraulic cement comprising a calcium silicate and at least one phosphate compound. The phosphate compound is included in an amount sufficient to react a major portion of the calcium hydroxide that is produced during hydration of the cement to hydroxyapatite or other calcium phosphates. The phosphate compound is preferably a mono-calcium phosphate. The cement is useful in both bio-medical/dental and engineering applications. The calcium hydroxide is reacted by the phosphate to form hydroxiapatite or other calcium phosphate that is co-precipitated with the calcium silicate hydrate to form a composite-like structure on a nano-scale level. The reduced calcium hydroxide content in the set cement increases its strength and reduces its pH. The hydroxiapatite content and the reduced pH render the cement bio-active and suitable for use in medical and dental implants, for example, for replacement bone and tooth material. Due to its high strength, the cement may also be used for structural/engineering applications.

Abstract: A hydraulic cement comprising a calcium silicate and at least one phosphate compound. The phosphate compound is included in an amount sufficient to react a major portion of the calcium hydroxide that is produced during hydration of the cement to hydroxyapatite or other calcium phosphates. The phosphate compound is preferably a mono-calcium phosphate. The cement is useful in both bio-medical/dental and engineering applications. The calcium hydroxide is reacted by the phosphate to form hydroxiapatite or other calcium phosphate that is co-precipitated with the calcium silicate hydrate to form a composite-like structure on a nano-scale level. The reduced calcium hydroxide content in the set cement increases its strength and reduces its pH. The hydroxiapatite content and the reduced pH render the cement bio-active and suitable for use in medical and dental implants, for example, for replacement bone and tooth material. Due to its high strength, the cement may also be used for structural/engineering applications.

Abstract: A hydraulic cement for biomedical applications. The cement sets in-situ, hardening when exposed to water to produce nano-dispersed composite of calcium-silicate-hydrate gel mixed with hydroxyapatite. In comparison with prior cements, the composition provides high biocompatibility, high bioactivity and high biomechanical strength, due to the composite structure of the calcium silicate hydrate reinforced with co-precipitated particles of hydroxyapatite. Biocompatibility is also increased due to an absence of aluminum and magnesium in the composition. The cement is suitable for variety of applications, including dental implants, bone fixation, and bone repair.

Abstract: A hydraulic cement for biomedical applications. The cement sets in-situ, hardening when exposed to water to produce nano-dispersed composite of calcium-silicate-hydrate gel mixed with hydroxyapatite. In comparison with prior cements, the composition provides high biocompatibility, high bioactivity and high biomechanical strength, due to the composite structure of the calcium silicate hydrate reinforced with co-precipitated particles of hydroxyapatite. Biocompatibility is also increased due to an absence of aluminum and magnesium in the composition. The cement is suitable for variety of applications, including dental implants, bone fixation, and bone repair.

Abstract: A hydraulic cement comprising a calcium silicate and at least one phosphate compound. The phosphate compound is included in an amount sufficient to react a major portion of the calcium hydroxide that is produced during hydration of the cement to hydroxyapatite or other calcium phosphates. The phosphate compound is preferably a mono-calcium phosphate. The cement is useful in both bio-medical/dental and engineering applications. The calcium hydroxide is reacted by the phosphate to form hydroxiapatite or other calcium phosphate that is co-precipitated with the calcium silicate hydrate to form a composite-like structure on a nano-scale level. The reduced calcium hydroxide content in the set cement increases its strength and reduces its pH. The hydroxiapatite content and the reduced pH render the cement bio-active and suitable for use in medical and dental implants, for example, for replacement bone and tooth material. Due to its high strength, the cement may also be used for structural/engineering applications.