Abstract: Techniques for silicide, germanide or germanosilicide formation in extremely small structures are provided. In one aspect, a method for forming a silicide, germanide or germanosilicide in a three-dimensional silicon, germanium or silicon germanium structure having extremely small dimensions is provided. The method includes the following steps. At least one element is implanted into the structure. At least one metal is deposited onto the structure. The structure is annealed to intersperse the metal within the silicon, germanium or silicon germanium to form the silicide, germanide or germanosilicide wherein the implanted element serves to prevent morphological degradation of the silicide, germanide or germanosilicide. The implanted element can include at least one of carbon, fluorine and silicon.

Abstract: Techniques for silicide, germanide or germanosilicide formation in extremely small structures are provided. In one aspect, a method for forming a silicide, germanide or germanosilicide in a three-dimensional silicon, germanium or silicon germanium structure having extremely small dimensions is provided. The method includes the following steps. At least one element is implanted into the structure. At least one metal is deposited onto the structure. The structure is annealed to intersperse the metal within the silicon, germanium or silicon germanium to form the silicide, germanide or germanosilicide wherein the implanted element serves to prevent morphological degradation of the silicide, germanide or germanosilicide. The implanted element can include at least one of carbon, fluorine and silicon.

Abstract: A method for forming a semiconductor-on-insulator (SOI) substrate is described incorporating the steps of heating a substrate, implanting oxygen into a heated substrate, cooling the substrate, implanting into a cooled substrate and annealing. The steps of implanting may be at several energies to provide a plurality of depths and corresponding buried damaged regions. Prior to implanting, the step of cleaning the substrate surface and/or forming a patterned mask thereon may be performed. The invention overcomes the problem of raising the quality of buried oxide and its properties such as surface roughness, uniform thickness and breakdown voltage Vbd.

Abstract: A method for forming a semiconductor-on-insulator (SOI) substrate is described incorporating the steps of heating a substrate, implanting oxygen into a heated substrate, cooling the substrate, implanting into a cooled substrate and annealing. The steps of implanting may be at several energies to provide a plurality of depths and corresponding buried damaged regions. Prior to implanting, the step of cleaning the substrate surface and/or forming a patterned mask thereon may be performed. The invention overcomes the problem of raising the quality of buried oxide and its properties such as surface roughness, uniform thickness and breakdown voltage Vbd.

Abstract: A method for forming a semiconductor-on-insulator (SOI) substrate is described incorporating the steps of heating a substrate, implanting oxygen into a heated substrate, cooling the substrate, implanting into a cooled substrate and annealing. The steps of implanting may be at several energies to provide a plurality of depths and corresponding buried damaged regions. Prior to implanting, the step of cleaning the substrate surface and/or forming a patterned mask thereon may be performed. The invention overcomes the problem of raising the quality of buried oxide and its properties such as surface roughness, uniform thickness and breakdown voltage Vbd.