Patents by Inventor Silvia Dahlund
Silvia Dahlund has filed for patents to protect the following inventions. This listing includes patent applications that are pending as well as patents that have already been granted by the United States Patent and Trademark Office (USPTO).
-
Patent number: 8343620Abstract: An ?-Al2O3 coated cutting tool insert combining a cemented carbide with a binder phase enriched surface zone and a textured ?-Al2O3-layer is disclosed. The ?-Al2O3 layer has a thickness ranging from about 2-9 ?m and is composed of columnar grains having a length/width ratio from about 2-12. It is characterized by a strong (104) growth texture and by low intensity of the (012), (110) and (113) diffraction peaks. The textured ?-Al2O3 is preferably deposited on an MTCVD Ti(C,N) layer having a thickness from about 2-10 ?m. When the alumina layer is the uppermost layer, it may be wet-blasted to an Ra value of <about 1 ?m, giving the tool a black and shiny appearance.Type: GrantFiled: January 29, 2008Date of Patent: January 1, 2013Assignee: Seco Tools ABInventors: Sakari Ruppi, Jenni Zackrisson, Silvia Dahlund
-
Publication number: 20110232433Abstract: A method of high-speed turning of metal using a cutting tool insert for turning of steel. The cutting tool insert includes a (006) textured ?-Al2O3 coated cemented carbide grade. The cemented carbide body has 4.5-6.5 wt-% Co and 3-10 wt-% cubic carbide forming metals and an S-value of 0.77-0.92 and a coercivity of 10-20 kA/m. The ?-Al2O3 layer has a thickness ranging from 7 to 12 ?m and is composed of columnar grains having a length/width ratio from 2 to 12 and is deposited on an MTCVD Ti(C,N) layer having a thickness from 4 to 12 ?m. The alumina layer is characterised by a pronounced (006) growth texture. The alumina layer is the uppermost layer and is wet-blasted having an Ra value of less than 1 ?m, giving the tool a black and shiny appearance.Type: ApplicationFiled: June 7, 2011Publication date: September 29, 2011Applicant: SECO TOOLS ABInventors: Jenni ZACKRISSON, Silvia DAHLUND, Tommy LARSSON
-
Patent number: 7985471Abstract: The present invention concerns a cutting tool insert for turning of steel at high cutting speeds. The cutting tool insert comprises a (006) textured ?-Al2O3 coated cemented carbide grade. The cemented carbide body has about 4.5-6.5 wt-% Co and about 3-10 wt-% cubic carbide forming metals and an S-value of about 0.77-0.92 and a coercivity of about 10-20 kA/m. The ?-Al2O3 layer has a thickness ranging from about 7 to 12 ?m and is composed of columnar grains having a length/width ratio from about 2 to 12 and is deposited on an MTCVD Ti(C,N) layer having a thickness from about 4 to 12 ?m. The alumina layer is characterized by a pronounced (006) growth texture. The alumina layer is the uppermost layer and is wet-blasted having an Ra value of less than 1 ?m, giving the tool a black and shiny appearance.Type: GrantFiled: July 7, 2008Date of Patent: July 26, 2011Assignee: Seco Tools ABInventors: Jenni Zackrisson, Silvia Dahlund, Tommy Larsson
-
Publication number: 20090028741Abstract: A coated cutting insert for metal machining, in particular of short chipping materials, includes a tungsten carbide-based substrate with a binder phase enriched surface zone having at least one rake face and at least one clearance face intersecting to form a cutting edge. The binder phase enriched surface zone is at least partly missing on the rake face including at least a part of the surface extending from the cutting edge. As a result, an optimum combination of edge strength and wear resistance has been achieved.Type: ApplicationFiled: September 12, 2008Publication date: January 29, 2009Applicant: SECO TOOLS ABInventors: Silvia Dahlund, Andreas Larsson
-
Publication number: 20090017289Abstract: The present invention concerns a cutting tool insert for turning of steel at high cutting speeds. The cutting tool insert comprises a (006) textured ?-Al2O3 coated cemented carbide grade. The cemented carbide body has about 4.5-6.5 wt-% Co and about 3-10 wt-% cubic carbide forming metals and an S-value of about 0.77-0.92 and a coercivity of about 10-20 kA/m. The ?-Al2O3 layer has a thickness ranging from about 7 to 12 ?m and is composed of columnar grains having a length/width ratio from about 2 to 12 and is deposited on an MTCVD Ti(C,N) layer having a thickness from about 4 to 12 ?m. The alumina layer is characterised by a pronounced (006) growth texture. The alumina layer is the uppermost layer and is wet-blasted having an Ra value of less than 1 ?m, giving the tool a black and shiny appearance.Type: ApplicationFiled: July 7, 2008Publication date: January 15, 2009Inventors: Jenni Zackrisson, Silvia Dahlund, Tommy Larsson
-
Patent number: 7435486Abstract: A coated cutting insert for metal machining, in particular of short chipping materials, includes a tungsten carbide-based substrate with a binder phase enriched surface zone having at least one rake face and at least one clearance face intersecting to form a cutting edge. The binder phase enriched surface zone is at least partly missing on the rake face including at least a part of the surface extending from the cutting edge. As a result, an optimum combination of edge strength and wear resistance has been achieved.Type: GrantFiled: June 20, 2005Date of Patent: October 14, 2008Assignee: Seco Tools ABInventors: Silvia Dahlund, Andreas Larsson
-
Publication number: 20080187775Abstract: An ?-Al2O3 coated cutting tool insert combining a cemented carbide with a binder phase enriched surface zone and a textured ?-Al2O3-layer is disclosed. The ?-Al2O3 layer has a thickness ranging from about 2-9 ?m and is composed of columnar grains having a length/width ratio from about 2-12. It is characterised by a strong (104) growth texture and by low intensity of the (012), (110) and (113) diffraction peaks. The textured ?-Al2O3 is preferably deposited on an MTCVD Ti(C,N) layer having a thickness from about 2-10 ?m. When the alumina layer is the uppermost layer, it may be wet-blasted to an Ra value of <about 1 ?m, giving the tool a black and shiny appearance.Type: ApplicationFiled: January 29, 2008Publication date: August 7, 2008Inventors: Sakari Ruppi, Jenni Zackrisson, Silvia Dahlund
-
Patent number: 7135221Abstract: A cutting tool insert with a cemented carbide and a coating. The cemented carbide substrate includes WC, 7 to 12 wt-% Co, 5 to 11 wt-% cubic carbides of metals from the groups IVb, Vb and VIb with a binder phase that is highly alloyed with cobalt. The tungsten carbide phase has a mean intercept length of 0.7 to 1.4 ?m. The coating includes at least one 2 to 12 ?m thick ?-Al2O3 layer composed of columnar grains with texture coefficients: TC(012)>2.2 and TC(024)>0.6×TC(012).Type: GrantFiled: October 27, 2004Date of Patent: November 14, 2006Assignee: Seco Tools ABInventors: Sakari Ruppi, Silvia Dahlund, Jenni Zackrisson
-
Publication number: 20060099433Abstract: A coated cutting insert for metal machining, in particular of short chipping materials, includes a tungsten carbide-based substrate with a binder phase enriched surface zone having at least one rake face and at least one clearance face intersecting to form a cutting edge. The binder phase enriched surface zone is at least partly missing on the rake face including at least a part of the surface extending from the cutting edge. As a result, an optimum combination of edge strength and wear resistance has been achieved.Type: ApplicationFiled: June 20, 2005Publication date: May 11, 2006Applicant: SECO TOOLS ABInventors: Silvia Dahlund, Andreas Larsson
-
Publication number: 20050129987Abstract: A cutting tool insert with a cemented carbide and a coating. The cemented carbide substrate includes WC, 7 to 12 wt-% Co, 5 to 11 wt-% cubic carbides of metals from the groups IVb, Vb and VIb with a binder phase that is highly alloyed with cobalt. The tungsten carbide phase has a mean intercept length of 0.7 to 1.4 ?m. The coating includes at least one 2 to 12 ?m thick ?-Al2O3 layer composed of columnar grains with texture coefficients: TC(012)>2.2 and TC(024)>0.6×TC(012).Type: ApplicationFiled: October 27, 2004Publication date: June 16, 2005Applicant: SECO TOOLS ABInventors: Sakari Ruppi, Silvia Dahlund, Jenni Zackrisson