Abstract: A powdered catalyst material on a titanium oxide basis. The powdered catalyst material includes a combined content of at least 90 wt.-% of a hydrated titanium oxide having the general formula TiO(2-x)(OH)2x, with 0<x?1, (calculated as TiO2), and a silicon dioxide and hydrated precursors of the silicon dioxide (calculated as SiO2). A weight ratio of TiO2/SiO2, determined for TiO2 and SiO2 respectively, is at least 3 and less than 30. The wt.-% is based on a total weight of the catalyst material after the catalyst material has been dried at 105° C. for at least 2 hours. The powdered catalyst material has a specific surface area of >300 m2/g and an isoelectric point of from 4.0 to 7.0.

Abstract: A TiO2-based catalyst precursor material in powder form includes TiO2 particles with the formula TiO(2-x)(OH)2x (x=0-1). The particles are coated with one or more auxiliary shaping agents and after coating and drying have a specific surface area of at least 150 m2/g. The material has a content of 1) 50-99.5% by weight of the titanium-oxygen compound with the general formula TiO(2-x)(OH)2x, wherein x=0 to 1, or mixtures thereof, wherein the crystalline phases of the titanium-oxygen compound are in the anatase form, and 2) 0.5-50% by weight of an auxiliary shaping agent or mixtures thereof, which evaporates, sublimates and/or decomposes upon heating to temperatures below the transformation temperature from anatase to rutile, wherein the % by weight are relative to the total weight of the dried catalyst precursor material.

Abstract: A powdered catalyst material on a titanium oxide basis. The powdered catalyst material includes a combined content of at least 90 wt.-% of a hydrated titanium oxide having the general formula TiO(2-x)(OH)2x, with 0<x?1, (calculated as TiO2), and a silicon dioxide and hydrated precursors of the silicon dioxide (calculated as SiO2). A weight ratio of TiO2/SiO2, determined for TiO2 and SiO2 respectively, is at least 3 and less than 30. The wt.-% is based on a total weight of the catalyst material after the catalyst material has been dried at 105° C. for at least 2 hours. The powdered catalyst material has a specific surface area of >300 m2/g and an isoelectric point of from 4.0 to 7.0.

Abstract: A catalyst material, more specifically a catalyst material based on TiO2/SiO2 in particulate form having a content of metal in the form of the metal oxide or metal oxide precursor, is used in chemical catalysis, especially for removal of pollutants, such as nitrogen oxides from combustion gases.

Abstract: A TiO2-based catalyst precursor material in powder form includes TiO2 particles with the formula TiO(2-x)(OH)2x (x=0-1). The particles are coated with one or more auxiliary shaping agents and after coating and drying have a specific surface area of at least 150 m2/g. The material has a content of 1) 50-99.5% by weight of the titanium-oxygen compound with the general formula TiO(2-x)(OH)2x, wherein x=0 to 1, or mixtures thereof, wherein the crystalline phases of the titanium-oxygen compound are in the anatase form, and 2) 0.5-50% by weight of an auxiliary shaping agent or mixtures thereof, which evaporates, sublimates and/or decomposes upon heating to temperatures below the transformation temperature from anatase to rutile, wherein the % by weight are relative to the total weight of the dried catalyst precursor material.

Abstract: A TiO2-based catalyst material in particle form having a content of metal removes pollutants, in particular of nitrogen oxides from combustion gases.

Abstract: The invention concerns a process for the production of a storage-stable barium sulphate, the barium sulphate produced thereby and the use thereof as an additive.

Abstract: A catalyst material, more specifically a catalyst material based on TiO2/SiO2 in particulate form having a content of metal in the form of the metal oxide or metal oxide precursor, to processes for preparation thereof and to the use thereof in chemical catalysis, especially for removal of pollutants, such as nitrogen oxides from combustion gases

Abstract: A TiO2-based catalyst material in particle form having a content of metal removes pollutants, in particular of nitrogen oxides from combustion gases.

Abstract: The invention concerns a process for preparing an additive for polymers, the additive itself and the use of the additive for improving the surface properties of polymers.

Abstract: The invention concerns a process for the production of a storage-stable barium sulphate, the barium sulphate produced thereby and the use thereof as an additive.

Abstract: The invention concerns a process for preparing an additive for polymers, the additive itself and the use of the additive for improving the surface properties of polymers.

Abstract: The invention provides titanium-dioxide-containing composites, a method for their production and the use of these composites.

Abstract: Titanium dioxide-containing composites, methods for producing them and the use of the composites.

Abstract: The invention relates to a method for producing barium sulphate having an organically modified surface, barium sulphate produced according to said method and to the use thereof.

Abstract: Barium sulfate-containing composites, to methods for producing them and methods of using of the composites, as well as components containing the composites.

Abstract: Barium sulfate-containing composites, to methods for producing the same and to the use of said composites.

Abstract: The invention relates to a method for producing barium sulphate having an organically modified surface, barium sulphate produced according to said method and to the use thereof.