Abstract: Phosphorus pentoxide production with fluorine management includes collecting phosphorus from kiln off gas as phosphoric acid containing fluorine and reacting the fluorine in the phosphoric acid with reactive silica to yield fluorosilicic acid. The fluorosilicic acid is removed from the collected phosphoric acid. Fluorine management includes discharging from the kiln a residue containing processed agglomerates and heating the discharged, processed agglomerates and releasing fluorine therefrom. The released fluorine is reacted with reactive silica to yield fluorosilicic acid and the fluorosilicic acid is collected. Fluorine management includes forming a reducing kiln bed with feed agglomerates below a reducing freeboard. Kiln off gas is generated containing phosphorus in the form of elemental phosphorus a) oxidized outside of the kiln to phosphorus pentoxide and collected as phosphoric acid, b) collected as elemental phosphorus, or c) both.

Abstract: A phosphorous pentoxide producing method includes forming pre-feed agglomerates containing phosphate ore particles, carbonaceous material particles, and silica particles and heating the pre-feed agglomerates in a reducing or inert atmosphere to an induration temperature from above 900 C to less than 1180 C and maintaining the induration temperature for 15 minutes or more. The method includes forming feed agglomerates and increasing a compression strength of the feed agglomerates to above 25 lbf using the heating, the feed agglomerates exhibiting a calcium-to-silica mole ratio less than 1 and a silica-to-(calcium+magnesium) mole ratio greater than 2. A reducing kiln bed is formed using the feed agglomerates, kiln off-gas is generated, and phosphorous pentoxide is collected from the kiln off gas.

Abstract: A phosphorous pentoxide producing method includes forming pre-feed agglomerates containing phosphate ore particles, carbonaceous material particles, and silica particles and heating the pre-feed agglomerates in a reducing or inert atmosphere to an induration temperature from above 900 C to less than 1180 C and maintaining the induration temperature for 15 minutes or more. The method includes forming feed agglomerates and increasing a compression strength of the feed agglomerates to above 25 lbf using the heating, the feed agglomerates exhibiting a calcium-to-silica mole ratio less than 1 and a silica-to-(calcium+magnesium) mole ratio greater than 2. A reducing kiln bed is formed using the feed agglomerates, kiln off-gas is generated, and phosphorous pentoxide is collected from the kiln off gas.