Abstract: This invention relates to homogeneous blends of: 1) from 60 to 99 weight percent of one or more semi-crystalline polymers (based upon the weight of the semi-crystalline and semi-amorphous polymers), each semi-crystalline polymer comprising propylene and from 0 to 5 weight % alpha-olefin comonomer (based upon the weight of the polymer), said semi-crystalline polymers each having a melting point between 100 and 170° C. and a melt flow rate of 200 dg/min or less; and 2) from 1 to 40 weight % of one or more semi-amorphous polymers (based upon the weight of the semi-crystalline and semi-amorphous polymers), each semi-amorphous polymer comprising propylene and from 5 to 12 weight % of one or more C2 and or C4 to C10 alpha-olefin comonomers, said semi-amorphous polymers each having: a) 10 to 50 percent crystallinity or less; b) a melt flow rate of 200 dg/min or less; c) a DSC melting point (second melt Tm) of 130° C.

Abstract: This invention relates to a molded article comprising a heterogeneous blend that includes: 1) from 60 to 99 weight percent of one or more semi-crystalline propylene homopolymers or copolymers having a melting point between 100 and 170 ° C. and a melt flow rate of 200 dg/min or less; and 2) from 1 to 40 weight % of one or more semi-amorphous propylene /C2 and/or C4 to C10 ?-olefin copolymers each having a particular heat of fusion, a melt flow rate, intermolecular compositional distribution as determined by thermal fractionation in hexane, Mw/Mn, and propylene triad tacticity such that the molded part formed from the resulting blend has improved notched impact strength, flexibility, elongation, and resistance to stress whitening at a thickness of from 250 ?pm to 10 mm.

Abstract: This invention relates to a nonwoven article comprising a heterogeneous blend comprising: 1) from 60 to 99 weight percent of one or more semi-crystalline polymers (based upon the weight of the semi-crystalline and semi-amorphous polymers), each semi-crystalline polymer comprising propylene and from 0 to 5 weight % alpha-olefin comonomer (based upon the weight of the polymer), said semi-crystalline polymers each having a melting point between 100 and 170° C. and a melt flow rate of 2000 dg/min or less; and 2) from 1 to 40 weight % of one or more semi-amorphous polymers (based upon the weight of the semi-crystalline and semi-amorphous polymers), each semi-amorphous polymer comprising propylene and from 10 to 25 weight % of one or more C2 and or C4 to C10 alpha-olefin comonomers, said semi-amorphous polymers each having: a) heat of fusion of 4 to 70 J/g; b) a Melt Flow Rate of 0.