Abstract: The invention relates to a method for manufacturing a foundry body including the preparation of a granular mixture including a polycondensed resin having modified formaldehyde, optionally incorporating an aromatic or polyaromatic during the synthesis thereof, a hardening agent, a formaldehyde sensor compound, water and optionally at least one resin selected from the group comprising tannins, natural polyphenols, and lignins, placing said granular mixture in contact with the surface of a forming tool, and insufflating a flow of gas at 50° C. to 380° C. into the granular mixture for 1 to 300 seconds, in order to ensure at least partial hardening of said mixture. The invention also relates to a method for manufacturing a molded foundry piece made of metal or a metal alloy, which includes pouring metal into at least one body (mold and/or core) thus produced; and to a foundry piece thus manufactured.

Abstract: The invention relates to a method for manufacturing a foundry body including the preparation of a granular mixture including a polycondensed resin having modified formaldehyde, optionally incorporating an aromatic or polyaromatic during the synthesis thereof, a hardening agent, a formaldehyde sensor compound, water and optionally at least one resin selected from the group comprising tannins, natural polyphenols, and lignins, placing said granular mixture in contact with the surface of a forming tool, and insufflating a flow of gas at 50° C. to 380° C. into the granular mixture for 1 to 300 seconds, in order to ensure at least partial hardening of said mixture. The invention also relates to a method for manufacturing a moulded foundry piece made of metal or a metal alloy, which includes pouring metal into at least one body (mould and/or core) thus produced; and to a foundry piece thus manufactured.

Abstract: The invention relates to a method for producing a body including: preparing a granular mixture including a) at least 90 wt % of mineral oxide grains; b) 0.3 to 3 wt % of resin polycondensed with formaldehyde and/or the derivatives thereof, the percentage being calculated in terms of dry resin extract; c) 0.001 to 1 wt % of a hardening agent, the percentage being calculated in terms of dry hardener extract; d) 0.005 to 0.35 wt % of a formaldehyde scavenger compound; and e) 0.2 to 3 wt % of water; contacting said granular mixture with a surface of a forming tool; and insufflating a gas flow at 50 to 380 degrees into the granular mixture for 1 to 300 seconds in order to at least partially cure said mixture, the formaldehyde scavenger being carbohydrazide.

Abstract: The invention relates to a method for producing a body including: preparing a granular mixture including a) at least 90 wt % of mineral oxide grains; b) 0.3 to 3 wt % of resin polycondensed with formaldehyde and/or the derivatives thereof, the percentage being calculated in terms of dry resin extract; c) 0.001 to 1 wt % of a hardening agent, the percentage being calculated in terms of dry hardener extract; d) 0.005 to 0.35 wt % of a formaldehyde scavenger compound; and e) 0.2 to 3 wt % of water; contacting said granular mixture with a surface of a forming tool; and insufflating a gas flow at 50 to 380 degrees into the granular mixture for 1 to 300 seconds in order to at least partially cure said mixture, the formaldehyde scavenger being carbohydrazide.