Abstract: The present invention refers to a high internal phase polyelectrolyte emulsions which are useful for the manufacture of superabsorbent polymers having two phases: i) a continuous oil phase and the ii) a dispersed aqueous phase containing the aqueous monomer solution prior to polymerization and the polyelectrolyte in water-soluble, or water-swellable or very slightly crosslinked form after polymerization, wherein the polymerization occurs in the dispersed aqueous phase and wherein the dispersed aqueous phase contains a high concentration of polyelectrolyte. The present invention also refers to a process for preparing such emulsions and for inverting these emulsions so as to form films or other patterns of the superabsorbent polymer. Absorbent structures containing SAP films or other patterns prepared by the present invention are also contemplated.

Abstract: A durable, conformable, absorbent, hydrophilic, polymeric latex foam composition having a free absorbent capacity of at least 5 grams of a 0.9 weight percent aqueous saline solution per gram of foam and capable of vertically wicking said aqueous saline solution to a height of greater than about 5 cm. In a preferred embodiment, after compression, the latex foam composition remains thin until wet, whereupon it expands and exhibits a high free absorbent capacity and high vertical wicking height.

Abstract: The present invention refers to a high internal phase polyclectrolyte emulsions which are useful for the manufacture of superabsorbent polymers having two phases: i) a continuous oil phase and the ii) a dispersed aqueous phase containing the aqueous monomer solution prior to polymerization and the polyelectrolyte in water-soluble, or water-swellable or very slightly crosslinked form after polymerization, wherein the polymerization occurs in the dispersed aqueous phase and wherein the dispersed aqueous phase contains a high concentration of polyclectrolyte. The present invention also refers to a process for preparing such emulsions and for inverting these emulsions so as to form films or other patterns of the superabsorbent polymer. Absorbent structures containing SAP films or other patterns prepared by the present invention are also contemplated.

Abstract: The present invention refers to a high internal phase polyelectrolyte emulsions which are useful for the manufacture of superabsorbent polymers having two phases: i) a continuous oil phase and the ii) a dispersed aqueous phase containing the aqueous monomer solution prior to polymerization and the polyelectrolyte in water-soluble, or water-swellable or very slightly crosslinked form after polymerization, wherein the polymerization occurs in the dispersed aqueous phase and wherein the dispersed aqueous phase contains a high concentration of polyelectrolyte.

Abstract: A durable, conformable, absorbent, hydrophilic, polymeric latex foam composition having a free absorbent capacity of at least 5 grams of a 0.9 weight percent aqueous saline solution per gram of foam and capable of vertically wicking said aqueous saline solution to a height of greater than about 5 cm. In a preferred embodiment, after compression, the latex foam composition remains thin until wet, whereupon it expands and exhibits a high free absorbent capacity and high vertical wicking height.

Abstract: A durable, conformable, absorbent, hydrophilic, polymeric latex foam composition having a free absorbent capacity of at least 5 grams of a 0.9 weight percent aqueous saline solution per gram of foam and capable of vertically wicking said aqueous saline solution to a height of greater than about 5 cm. In a preferred embodiment, after compression, the latex foam composition remains thin until wet, whereupon it expands and exhibits a high free absorbent capacity and high vertical wicking height.

Abstract: High internal phase emulsions (HIPEs), porous polymeric materials made therefrom, and methods for making and using the same. Specific embodiments of the invention include water-in-oil high internal phase emulsions having at least 70 volume percent of an internal aqueous phase and less than 30 volume percent of an external oil phase wherein the oil phase comprises a vinyl polymerizable monomer and a surfactant effective to stabilize the emulsion. The subject surfactants are oil soluble and preferably include an oxyalkylene component.

Abstract: The invention comprises a fully continuous process for shaping a high internal phase emulsion (HIPE) with a polymerizable continuous phase into dry foam, comprising 1) providing a high internal phase emulsion (HIPE) comprising (a) at least 70 percent by volume of an eternal phase comprising one or more polymerizable monomer; (b) a surfactant in an amount effective to produce a high internal phase emulsion; and (c) an internal phase; 20 depositing the emulsion onto a lower moving support substrate; 3) leveling the emulsion to a desired thickness above the support substrate; 4) polymerizing the monomers by running the emulsion and the lower moving support substrate through a heating zone for a time sufficient to polymerize at least 75% of the monomer in the HIPE by the end of the heating zone; and 5) drying the polymerized HIPE in a drying zone for a time sufficient to produce a foam having greater than 50% of the internal phase removed.

Abstract: High internal phase emulsions (HIPEs), porous polymeric materials made therefrom, and methods for making and using the same. Specific embodiments of the invention include water-in-oil high internal phase emulsions having at least 70 volume percent of an internal aqueous phase and less than 30 volume percent of an external oil phase wherein the oil phase comprises a vinyl polymerizable monomer and a surfactant effective to stabilize the emulsion. The subject surfactants are oil soluble and preferably include an oxyalkylene component.

Abstract: High internal phase emulsions having an internal aqueous phase of greater than 70 percent by volume and an external oil phase comprising a vinyl polymerizable monomer contain a surfactant capable of chemically binding to the polymerizable monomer. Polymeric foams having a high internal phase emulsion stabilizing surfactant chemically bound to the polymeric material and a liquid capacity of from about 70 to 99 percent of its saturated volume can be prepared from such emulsions.