Abstract: The present invention is directed to a polypropylene composition (C) a melt flow rate MFR2 (230° C.) determined according to ISO 1133 in the range of 15 to 40 g/10 min, the use of said polypropylene composition (C) for the production of a foamed article and a foamed article comprising said polypropylene composition (C).

Abstract: Composition suitable for automotive application obtainable by blending at least components a) to f) a) 5.0 to 45 wt.-%, preferably 9.0 to 42 wt. %, more preferably 10 to 40 wt.-% of a first heterophasic polypropylene copolymer (HECO 1) b) 2.0 to 20 wt.-%, preferably 2.5 to 18 wt.-%, more preferably 3.0 to 17 wt.-% of a second heterophasic polypropylene copolymer (HECO 2) c) 10 to 60 wt.-%, preferably 12 to 55 wt.-%, more preferably 14 to 52 wt.-% of a polypropylene-polyethylene blend (A) d) 2.5 to 25 wt.-%, preferably 5.0 to 22 wt.-% and more preferably 6.5 to 20 wt.-% of an ethylene based elastomer e) 5.0 to 30 wt.-%, preferably 7.0 to 25 wt.-% and more preferably 8.5 to 20 wt.-% of an inorganic filler f) 0.1 to 4.0 wt.-% of additives.

Abstract: Upgraded polypropylene—polyethylene blend including random polypropylene copolymer and ethylene based plastomer.

Abstract: A composition suitable for automotive application obtainable by blending at least components a) to f), or a), b), c), d), C and f) under the proviso that e) is not present a) 12 to 40 wt.-%, preferably 14 to 38 wt. %, more preferably 15 to 35 wt.-% of a first heterophasic polypropylene copolymer (HECO 1) b) 12 to 40 wt.-%, preferably 14 to 38 wt.-%, more preferably 15 to 35 wt.-% of a second heterophasic polypropylene copolymer (HECO 2) c) 15 to 65 wt.-%, preferably 18 to 60 wt.-%, more preferably 20 to 55 wt.-% of a polypropylene-polyethylene blend (A) d) 3.0 to 20 wt.-%, preferably 5.0 to 15 wt.-% and more preferably 6.0 to 15 wt.-% of an inorganic filler e) 0 to 15 wt.-% HDPE f) 0.01 to 4.0 wt.-% of additives.

Abstract: A mixed-plastic-polyethylene composition having a melt flow rate (ISO 1133, 2.16 kg, 190° C.) of from 0.1 to 0.9 g/10 min and a density of from 956 kg/m3 to 970 kg/m3 comprising recycled polyolefin.

Abstract: Mixed-plastic-polyethylene composition having a melt flow rate (ISO 1133, 2.16 kg, 190° C.) of from 0.1 to 0.9 g/10 min; and a density of from 956 kg/m3 to 970 kg/m3, preferably from 958 to 968 kg/m3.

Abstract: A polyolefin composition (C) obtainable by blending: a recycling blend (A) with a virgin polypropylene homopolymer and optionally a virgin high density polyethylene.

Abstract: Mixed-plastic-polyethylene composition having a melt flow rate (ISO 1133, 2.16 kg, 190° C.) of from 0.2 to 0.7 g/10 min; and a density of from 956 to 965 kg/m3, preferably from 958 to 964 kg/m3.

Abstract: A polyethylene-polypropylene composition obtainable by blending a) 80 to 97 wt.-% of a blend (A) comprising A-1) polypropylene and A-2) polyethylene, wherein the ratio of polypropylene to polyethylene is from 3:7 to 13:7, and wherein blend (A) is a recycled material, which is recovered from a waste plastic material derived from post-consumer and/or post-industrial waste; and b) 3 to 20 wt.-% of a compatibilizer (B) being a heterophasic random copolymer comprising a random polypropylene copolymer matrix phase and an elastomer phase dispersed therein, whereby the heterophasic random copolymer has—a xylene insolubles content (XCI) of from 65 to 88 wt.-% (ISO 16152, led, 25° C.), and—a xylene soluble content XCS of 12 to 35 wt.-% (ISO 16152, led, 25° C.), the XCS fraction having an intrinsic viscosity (measured in decalin according to DIN ISO 1628/1 at 135° C.) of 1.2 dl/g to less than 3.0 dl/g, and—a flexural modulus of from 300 to 600 MPa (ISO 178, measured on injection moulded specimens, 23° C.

Abstract: The present invention relates to a mixed-plastic-polyethylene composition comprising: —a total amount of ethylene units (C2 units) of from 90.00 to 99.00 wt %, and—a total amount of continuous units having 3 carbon atoms corresponding to polypropylene (continuous C3 units) of from 0.01 to 5.00 wt %, with the total amounts of C2 units and continuous C3 units being based on the total weight amount of monomer units in the composition and measured according to quantitative 13C{1H} NMR measurement, and wherein the composition has—a melt flow rate (ISO 1133, 2.16 kg, 190° C.) of from 0.1 to 2.0 g/10 min; and—a density of from 930 kg/m3 to 955 kg/m3, preferably from 932 to 953 kg/m3, a process for producing said mixed-plastic-polyethylene composition, an article comprising said mixed-plastic-polyethylene composition and the use of said mixed-plastic-polyethylene composition for producing a cable layer.

Abstract: The present invention is directed to a polyethylene-polypropylene composition comprising a blend (A) being a recycled material, said blend comprising polypropylene and polyethylene, and a compatibilizer (B) being a copolymer of 1-butene and ethylene. Further, the present invention is directed to an article comprising said polyethylene-polypropylene composition and a process for preparing said polyethylene-polypropylene composition. The present invention is also directed to the use of a compatibilizer (B) being a copolymer of 1-butene and ethylene for improving the impact-stiffness balance and the morphology of the blend (A).

Abstract: A polyolefin composition obtainable by blending a) 96.0 to 99.7 wt.-% of a blend (A), being a recycled material comprising A-1) 30 to 70 wt.-% isotactic polypropylene homopolymer, A-2) 20 to 50 wt.-% polyethylene and ethylene containing copolymers, A-3) 0.5 to 4.0 wt.-% polyamide-6,various optional components, A-11) 1 ppm to 100 ppm of limonene, and A-12) 1 ppm to 200 ppm total fatty acid content with a maleic anhydride-grafted SEBS block copolymer, characterized by its melt volume rate and maleic anhydride content.

Abstract: The present invention relates to a polypropylene composition, an injection molded article comprising the polypropylene composition, a foamed article comprising the polypropylene composition as well as the use of a polypropylene homopolymer (H-PP1) for reducing the 5stiffness reduction factor of a foamed injection molded article by at least 40 as determined by the difference of the flexural modulus measured according to ISO 178 of the non-foamed and foamed injection molded article and compared to an article comprising the same amount of a polypropylene which has been polymerized in the presence of a Ziegler-Natta catalyst.

Abstract: The present invention is directed to a polyethylene-polypropylene composition comprising a blend (A) being a recycled material, said blend comprising polypropylene and polyethylene, and a compatibilizer (B) being a C2C3C4 terpolymer. Further, the present invention is directed to an article comprising said polyethylene-polypropylene composition and a process for preparing said polyethylene-polypropylene composition. The present invention is also directed to the use of a compatibilizer (B) being a C2C3C4 terpolymer for improving the impact-stiffness balance and the morphology of the blend (A).

Abstract: The present invention is directed to a polyethylene-polypropylene composition comprising a blend (A) being a recycled material, said blend comprising polypropylene and polyethylene, and a compatibilizer (B) being a copolymer of 1-butene and ethylene. Further, the present invention is directed to an article comprising said polyethylene-polypropylene composition and a process for preparing said polyethylene-polypropylene composition. The present invention is also directed to the use of a compatibilizer (B) being a copolymer of 1-butene and ethylene for improving the impact-stiffness balance and the morphology of the blend (A).

Abstract: The present invention is directed to the use of a polypropylene composition comprising at least one heterophasic polypropylene and a filler for the production of at least partially painted articles which show both a good paintability and a good surface appearance; and the painted articles produced therefrom. Further the invention is directed to a polypropylene composition showing improved surface appearance and paintability.

Abstract: The present invention is directed to a polypropylene composition (C) comprising a heterophasic propylene copolymer (HECO1) having an intrinsic viscosity (IV) of the xylene soluble fraction (XCS) above 3.5 dl/g, an inorganic filler (F) and a nucleating agent (NU) being a dicarboxylic acid and/or a salt thereof. Further, the present invention is directed to the use of said polypropylene composition (C) for the production of a foamed article as well as a foamed article comprising said polypropylene composition (C). The present invention is also directed to the use of a nucleating agent (NU) being dicarboxylic acid and/or a salt thereof for the reduction of tigerskin of a polypropylene composition.

Abstract: A polyethylene-polypropylene composition obtainable by blending a) 80 to 97 wt.-% of a blend (A) comprising A-1) polypropylene and A-2) polyethylene, wherein the weight ratio of polypropylene to polyethylene is from 3:7 to 7:3, and wherein blend (A) is a recycled material, which is recovered from a waste plastic material derived from post-consumer and/or industrial waste; and b) 3 to 20 wt.-% of a compatibilizer (B) being a C2C8 plastomer, having—a DSC melting point of below 75° C. (ISO11357);—an MFR2 (ISO1133, 2.16 kg load at 190° C.) of equal or below 1.5 g/10 min; and—a density of equal or lower than 885 kg/m3 (ISO1183),wherein the ratio of MFR2 (blend (A) (ISO1133, 2.16 kg load at 230° C.)/MFR2(compatibilizer (B) (ISO1133, 2.16 kg load at 190 ° C.), is in the range 3.0 to 15; and c) 0 to 1.0 wt.-% of a stabilizer or mixture of stabilizers.

Abstract: A polypropylene-polyethylene composition obtainable by blending a) 80 to 97 wt.-% of a blend (A) comprising A-1) polypropylene and A-2) polyethylene, wherein the weight ratio of polypropylene to polyethylene is from 9:1 to 13:7, and wherein blend (A) is a recycled material, which is recovered from waste plastic derived from post-consumer and/or post-industrial waste; and b) 3 to 20 wt.-% of a compatibilizer (B) being a heterophasic random copolymer comprising a random polypropylene copolymer matrix phase and an elastomer phase dispersed therein, whereby the heterophasic random copolymer has—a xylene insoluble content XCI of 65 to 88 wt.-% (ISO 16152, led, 25° C.), —a xylene soluble content XCS of 12 to 35 wt.-% (ISO 16152, led, 25° C.), the XCS fraction having an intrinsic viscosity (measured in decalin according to DIN ISO 1628/1 at 135° C.) of 1.2 dl/g to less than 3.0 dl/g, and—a flexural modulus of from 300 to 600 MPa (ISO 178, measured on injection moulded specimens, 23° C.

Abstract: The present invention relates to a polyolefin composition, the use of the polyolefin composition in a compound with one or more virgin polymers for automotive articles or applications, pipes or profiles for construction applications, the use of a heterophasic polypropylene (HECO) as compatibilizer for polyolefin blends A) between a copolymer of ethylene and one or more C4 to C19 alpha olefin B) and a reinforcing mineral filler D) as well as a process for producing the polyolefin composition.