Abstract: Disclosed is a method for preparing hydrogen-rich fuel gas, including adding aluminum smelting waste residues into medium strong acid and soaking for 2-4 h, filtering and baking an obtained precipitate at 300-400° C. for 3-6 h to obtain pre-treated aluminum smelting waste residues; adding the waste residues into weak acid and performing ultrasonic treatment, performing centrifugal separation on an aluminum ash solution, baking for 3-6 h at a constant temperature of 400-500° C. in an air atmosphere, and naturally cooling to room temperature to obtain a cracking catalyst; uniformly mixing the cracking catalyst and biomass with a mass ratio of 1:1 and adding into a first-stage pyrolyzing furnace under N2 atmosphere, and heating from room temperature to 500-900° C. to obtain first-stage pyrolysis gas; and entering the first-stage pyrolysis gas into a second-stage pyrolyzing furnace for secondary catalytic cracking, so as to obtain hydrogen-rich fuel gas.

Abstract: The present disclosure discloses flake metal lithium powder and a preparing method thereof; by ultrasonically pulverizing the metal lithium placed in a low-viscosity inert organic resolvent using a vacuum ultrasonic pulverization method, a micrometer scale flake metal lithium powder is prepared. The metal lithium powder may be used as an anode material for a lithium cell or lithium ion cell. The present method has advantages of high product purity, simple operation, low processing temperature, low cost, high efficiency, and less demanding on equipment, etc., and has a high prospect of being applied to mass production of metal lithium powder.

Abstract: The present disclosure discloses flake metal lithium powder and a preparing method thereof; by ultrasonically pulverizing the metal lithium placed in a low-viscosity inert organic resolvent using a vacuum ultrasonic pulverization method, a micrometer scale flake metal lithium powder is prepared. The metal lithium powder may be used as an anode material for a lithium cell or lithium ion cell. The present method has advantages of high product purity, simple operation, low processing temperature, low cost, high efficiency, and less demanding on equipment, etc., and has a high prospect of being applied to mass production of metal lithium powder.