Abstract: A bimodal polyethylene composition, products made therefrom, methods of making and using same, and articles, including bottle caps and closures, containing same.

Abstract: An activator-nucleator formulation comprising an activating effective amount of (A) an alkylaluminum(chloride) compound (compound (A)); and a nucleating effective amount of a compound (B) selected from at least one of compounds (B1) to (B3): (B1) calcium (1R,2S)-cis-cyclohexane-1,2-dicarboxylate (1:1); (B2) calcium stearate (1:2), and (B3) zinc stearate (1:2); wherein the compound (A) is effective for activating a Ziegler-Natta procatalyst to give a Ziegler-Natta catalyst; and wherein the compound (B) is effective for lowering isothermal crystallization peak time period of a semicrystalline polyethylene polymer made in a polymerization process by the Ziegler-Natta catalyst. A method of polymerizing ethylene, and optionally 0, 1, or more alpha-olefin comonomers, in a polymerization process conducted in a polymerization reactor, the method comprising contacting ethylene, and optionally 0, 1, or more alpha-olefin comonomers, with the Ziegler-Natta catalyst system to give a semicrystalline polyethylene polymer.

Abstract: Provided are bimodal linear low density polyethylene copolymers (B-LLDPE copolymers) that have a combination of improved properties comprising at least one processability characteristic similar or better than that of an unblended monomodal ZN-LLDPE and a dart impact property similar or better than that of an unblended monomodal MCN-LLDPE. For the various aspects, the B-LLDPE copolymer has a density from 0.8900 to 0.9300 g/cm3; a melt index (I2) from 0.1 g/10 min. to 5 g/10 min.; a Mz from 600,000 to 1,200,000 g/mol; and a hexane extractables content present in a value of up to 2.6 wt. % as measured according to ASTM D-5227:95. The B-LLDPE copolymer can be further characterized by a first melt flow ratio (I21/I2) from 25 to 65 and a first molecular weight ratio (Mz/Mw) from 3.5 to 5.5.

Abstract: Provided are bimodal linear low density polyethylene copolymers (B-LLDPE copolymers) that have a combination of improved properties comprising at least one processability characteristic similar or better than that of an unblended monomodal ZN-LLDPE and a dart impact property similar or better than that of an unblended monomodal MCN-LLDPE. For the various aspects, the B-LLDPE copolymer has a density from 0.8900 to 0.9300 g/cm3; a melt index (I2) from 0.1 g/10 min. to 5 g/10 min.; a Mz from 600,000 to 1,900,000 g/mol; and a SHI from 5.35 to 75 ?*(1.0)/?*(100). The B-LLDPE copolymer can be further characterized by a first melt flow ratio (I21/I2) from 32 to 140 and a first molecular weight ratio (Mz/Mw) from 4.5 to 11.

Abstract: A spray-dried zirconocene catalyst system comprising a zirconocene catalyst and a hydrophobic fumed silica, which supports the zirconocene catalyst. A spray-drying method of making same. Polyolefins; methods of making and using same; and articles containing same.

Abstract: A nucleating agent-free and LLDPE-free polyolefin composition for making films with enhanced barrier properties against water vapor and oxygen gas. Related aspects include formulations, manufactured articles, films, and methods.

Abstract: A polyethylene blend comprising a uniform dispersion of constituents (A) and (B): (A) a Ziegler-Natta catalyst-made linear low density polyethylene and (B) a metallocene catalyst-made linear low density polyethylene, a composition comprising the polyethylene blend and at least one additive, methods of making and using same, and manufactured articles and films comprising or made from same.

Abstract: A polyethylene blend that has an improved stretch break property and is useful for stretch wrap film applications. The polyethylene blend consists essentially of approximately 98 weight percent (wt %) of a linear low-density polyethylene (LLDPE) component and approximately 2 wt % of a higher molecular weight high-density polyethylene polymer (HMW HDPE) component, based on the combined weight of the LLDPE and HMW HDPE components. Also, a method of making the polyethylene blend, a formulation comprising the polyethylene blend and at least one additive that is different than the polyethylene blend, a method of making a manufactured article from the polyethylene blend or formulation; the manufactured article made thereby, and use of the polyethylene blend for stretch wrapping object(s) in need thereof.

Abstract: A polyethylene blend comprising a uniform dispersion of constituents (A) and (B): (A) a Ziegler-Natta catalyst-made linear low density polyethylene and (B) a metallocene catalyst-made linear low density polyethylene, a composition comprising the polyethylene blend and at least one additive, methods of making and using same, and manufactured articles and films comprising or made from same.

Abstract: A bimodal linear polyethylene composition, products made therefrom, methods of making and using same, and articles containing same.

Abstract: An ethylene/1-hexene copolymer has a density from 0.9541 to 0.9600 gram per cubic centimeter (g/cm3), a molecular mass dispersity (DM=Mw/Mn) from greater than 2.0 to 3.5; and a Z-average molecular weight (Mz) from 120,000 to 240,000 grams per mole (g/mol). Methods of making and using same. Articles containing same.

Abstract: A multilayer blown film having an inner layer, a first outer layer, and a second outer layer, wherein the inner layer comprises an ethylene-based polymer having a MWCDI value greater than 0.9, and a melt index ratio (I10/I2) that meets the following equation: I10/I2?7.0?1.2×log (I2); and the first outer layer and the second outer layer independently comprise a polyethylene composition which comprises the reaction product of ethylene and, optionally, one or more alpha olefin comonomers, wherein the polyethylene composition is characterized by the following properties: (a) a melt index, I2, of from 0.1 to 2.0 g/10 min; (b) a density of from 0.910 to 0.930 g/cc; (c) a melt flow ratio, I10/I2, of from 6.0 to 7.6; and (d) a molecular weight distribution, (Mw/Mn) of from 2.5 to 4.0.

Abstract: An activator-nucleator formulation comprising an activating effective amount of (A) an alkylaluminum(chloride) compound (compound (A)); and a nucleating effective amount of a compound (B) selected from at least one of compounds (B1) to (B3): (B1) calcium (1R,2S)-cis-cyclohexane-1,2-dicarboxylate (1:1); (B2) calcium stearate (1:2), and (B3) zinc stearate (1:2); wherein the compound (A) is effective for activating a Ziegler-Naha procatalyst to give a Ziegler-Natta catalyst; and wherein the compound (B) is effective for lowering isothermal crystallization peak time period of a semicrystalline polyethylene polymer made in a polymerization process by the Ziegler-Natta catalyst. A method of polymerizing ethylene, and optionally 0, 1, or more alpha-olefin comonomers, in a polymerization process conducted in a polymerization reactor, the method comprising contacting ethylene, and optionally 0, 1, or more alpha-olefin comonomers, with the Ziegler-Naha catalyst system to give a semicrystalline polyethylene polymer.

Abstract: A carbon black-containing bimodal polyethylene composition, products made therefrom, methods of making and using same, and articles containing same.

Abstract: A bimodal polyethylene composition, products made therefrom, methods of making and using same, and articles, including bottle caps and closures, containing same.

Abstract: A spray-dried zirconocene catalyst system comprising a zirconocene catalyst and a hydrophobic fumed silica, which supports the zirconocene catalyst. A spray-drying method of making same. Polyolefins; methods of making and using same; and articles containing same.

Abstract: An ethylene/1-hexene copolymer has a density from 0.9541 to 0.9600 gram per cubic centimeter (g/cm3), a molecular mass dispersity (ÐM=Mw/Mn) from greater than 2.0 to 3.5; and a Z-average molecular weight (Mz) from 120,000 to 240,000 grams per mole (g/mol). Methods of making and using same. Articles containing same.

Abstract: A polyethylene blend comprising a uniform dispersion of constituents (A) and (B): (A) a Ziegler-Natta catalyst-made linear low density polyethylene and (B) a metallocene catalyst-made linear low density polyethylene, a composition comprising the polyethylene blend and at least one additive, methods of making and using same, and manufactured articles and films comprising or made from same.

Abstract: A polyethylene blend comprising a uniform dispersion of constituents (A) and (B): (A) a Ziegler-Natta catalyst-made linear low density polyethylene and (B) a metallocene catalyst-made linear low density polyethylene, a composition comprising the polyethylene blend and at least one additive, methods of making and using same, and manufactured articles and films comprising or made from same.

Abstract: A bimodal linear polyethylene composition, products made therefrom, methods of making and using same, and articles containing same.