Abstract: A submerged arc welding method for a high strength (2.25%-3%)Cr-3% Mo-V steel, to obtain a weld metal excellent in strength at room temperature and high temperature, toughness, and creep strength, after SR, temper brittleness resistance, cold crack resistance and SR crack resistance. The Cr-Mo steel contains: 2.00 to 3.25% of Cr, 0.90 to 1.20% of Mo, and V as essential components, and Nb, Ti, B and Ca as needed. A welding heat input is in the range of from 20 to 50 kJ/cm. The solid wire contains 0.09 to 0.19% of C, 0.30% or less of Si, 0.50 to 1.40% of Mn, 2.00 to 3.80% of Cr and 0.90 to 1.20% of Mo. The bonded flux contains 5 to 20% of SiO.sub.2, 20 to 40% of MgO, 2.4 to 12% of a metal fluoride (F-converted value) and 3 to 12% of a metal carbonate (CO.sub.2 -converted value). A weld metal contains 0.08 to 0.15% of C, 0.05 to 0.30% of Si, 0.50 to 1.20% of Mn, 0.030 to 0.060% of O, 0.10 to 0.50% of V and 0.005 to 0.035% of Nb. P and Ti in the weld metal are restricted to 0.010% or less and 0.