Abstract: A fiber of sea-islands phase separation wherein the sea component comprises a vinyl alcohol based polymer with high orientation and great crystallinity and the islands component comprises a water-insoluble cellulose based polymer with excellent absorptivity of alkaline solutions, thermal resistance and heat fusion resistance, and wherein the size of the islands is 0.03 to 10 .mu.m and the strength is 3 g/d or more, is readily disintegrated into a fibril of a diameter of 0.05 to 8 .mu.m when a mechanical stress is imposed onto the fiber wet in water.From the fibril with good hydrophilicity, high strength, great particle captivity and excellent reinforcing performance, and additionally with good absorptivity of alkaline solutions and great thermal resistance and heat fusion resistance, none of the fiber components therein is solubilized during fibrillation. Neither a beating process nor a beating solution causes foaming or environmental pollution.

Abstract: A fiber of sea-islands phase separation wherein the sea component comprises a vinyl alcohol based polymer with high orientation and great crystallinity and the islands component comprises a water-insoluble cellulose based polymer with excellent absorptivity of alkaline solutions, thermal resistance and heat fusion resistance, and wherein the size of the islands is 0.03 to 10 .mu.m and the strength is 3 g/d or more, is readily disintegrated into a fibril of a diameter of 0.05 to 8 .mu.m when a mechanical stress is imposed onto the fiber wet in water. From the fibril with good hydrophilicity, high strength, great particle captivity and excellent reinforcing performance, and additionally with good absorptivity of alkaline solutions and great thermal resistance and heat fusion resistance, none of the fiber components therein is solubilized during fibrillation. Neither a beating process nor a beating solution causes foaming or environmental pollution.

Abstract: A fiber of sea-islands phase separation wherein the sea component comprises a vinyl alcohol based polymer with high orientation and great crystallinity and the islands component comprises a water-insoluble cellulose based polymer with excellent absorptivity of alkaline solutions, thermal resistance and heat fusion resistance, and wherein the size of the islands is 0.03 to 10 .mu.m and the strength is 3 g/d or more, is readily disintegrated into a fibril of a diameter of 0.05 to 8 .mu.m when a mechanical stress is imposed onto the fiber wet in water.From the fibril with good hydrophilicity, high strength, great particle captivity and excellent reinforcing performance, and additionally with good absorptivity of alkaline solutions and great thermal resistance and heat fusion resistance, none of the fiber components therein is solubilized during fibrillation. Neither a beating process nor a beating solution causes foaming or environmental pollution.

Abstract: By dissolving a vinyl alcohol polymer (A) and an incompatible vinyl polymer (B), preferably an acrylonitrile polymer in a common solvent to prepare a spinning stock solution of a phase separation structure wherein the polymer (B) is present at particle sizes of 2 to 50 .mu.m, and wet spinning or dry-wet spinning the resulting spinning stock solution in a solidifying bath containing a mixture of an organic solvent capable of solidifying both the polymers (A) and (B) and the solvent of the spinning stock solution at a weight ratio of 25/75 to 85/15, thereby drawing the resulting yarn by 8-fold or more, a fiber is provided; and from the fiber can be produced a fibril with good hydrophilicity, a higher strength, and excellent heat fusion resistance, along with excellent wiping performance, filtering performance, micro-particle capturing properties and reinforcing performance, readily, stably and inexpensively.

Abstract: By mixing a high-melting polyvinyl alcohol type polymer (A) and a low-melting water-soluble polymer (B) in a solvent for the polymer (A) to prepare a spinning solution and then subjecting the solution to low-temperature spinning so that the resulting filaments are solidified uniformly in the cross-sectional direction, there is formed a fiber of sea-islands structure comprising said high-melting polyvinyl alcohol type polymer (A) as the sea component and said low-melting water-soluble polymer (B) as the islands component. In this fiber, at least part of the islands component is present in a fiber zone ranging from the fiber surface to 2 .mu.m inside and the fiber surface contains substantially no islands component. This fiber ordinarily shows the performance of the matrix phase, i.e.

Abstract: The process of the present invention comprises wet spinning or dry-jet-wet spinning a PVA-based polymer soluble in water at not more than 100.degree. C. while using a dope solvent and a solidifying solvent each comprising an organic solvent, wet drawing the solidified filaments, subjecting the drawn filaments to extraction treatment and then drying, and further subjecting the filaments to heat shrinking treatment under multi-stage temperature elevation condition. The water soluble fibers of the present invention obtained by this process, while having a low water dissolution temperature of not more than 100.degree. C., have a markedly small maximum shrinkage in water and has high tensile strength and small ash content. The water soluble fibers of the present invention are suitably used for chemical lace base fabrics and blended yarns with wool or jute.

Abstract: High-strength polyvinyl alcohol fiber is provided by extruding a polyvinyl alcohol dope solution through a spinneret into a coagulating bath, the spinneret being located such that substantially only its dope-extruding surface contacts the coagulating bath. This process can produce stably and at a low cost polyvinyl alcohol fibers with excellent strength.