Abstract: An epsilon iron oxide has an average particle size of 10 to 18 nm, a part of the iron element being substituted with a substitutional element and has a coercive force of 14 kOe or less, wherein a coefficient of variation of the particle size is 40% or less. A method for producing the same, a magnetic coating material and a magnetic recording medium using the epsilon iron oxide, includes depositing a metal compound of a substitutional element on iron oxide hydroxide to thereby obtain iron oxide hydroxide on which the metal compound is deposited; coating the iron oxide hydroxide on which the metal compound is deposited, with silicon oxide to thereby obtain iron oxide hydroxide coated with the silicon oxide; and applying heat treatment to the silicon oxide-coated iron oxide hydroxide in an oxidizing atmosphere, wherein a part of an iron element is substituted with the substitutional element.

Abstract: An epsilon iron oxide has an average particle size of 10 to 18 nm, a part of the iron element being substituted with a substitutional element and has a coercive force of 14 kOe or less, wherein a coefficient of variation of the particle size is 40% or less. A method for producing the same, a magnetic coating material and a magnetic recording medium using the epsilon iron oxide, includes depositing a metal compound of a substitutional element on iron oxide hydroxide to thereby obtain iron oxide hydroxide on which the metal compound is deposited; coating the iron oxide hydroxide on which the metal compound is deposited, with silicon oxide to thereby obtain iron oxide hydroxide coated with the silicon oxide; and applying heat treatment to the silicon oxide-coated iron oxide hydroxide in an oxidizing atmosphere, wherein a part of an iron element is substituted with the substitutional element.