Abstract: A coated article is obtained by electrodeposition coating using an electrodeposition coating composition, which comprises: (A) a resin component obtained by reacting an epoxy resin, an amino compound and/or a phenolic compound; (B) a resin component having a specific structural unit; (C) a blocked polyisocyanate compound; and (D) at least one rust inhibiting component selected from the group consisting of metal ions selected from zirconium, titanium, cobalt, vanadium, tungsten and molybdenum, oxymetal ions of the metal, and fluorometal ions of the metal.

Abstract: Objects of the present invention is to provide a zinc-based alloy electroplated film having a high corrosion resistance comparable to Zn—Cr alloy plating without containing chromium which gives a heavy environmental load, and a plated metal material using the same. The present invention relates to a zinc-based alloy electroplated film excellent in corrosion resistance containing (A) 30 to 96% by weight of zinc, (B) 2 to 20% by weight of an iron-group metal, and (C) 2 to 50% by weight of tungsten.

Abstract: This invention provides a method for forming multi-layered coating film excelling in appearance, corrosion resistance and chipping resistance, which comprises applying a first coloring paint (B), second coloring paint (C) and clear paint (D) onto cured coating film of a specific electrodeposition paint (A) of low weight loss under heating, wet-on-wet by the order stated; and heat-curing the three-layered coating film simultaneously.

Abstract: A coated article is obtained by electrodeposition coating using an electrodeposition coating composition, which comprises: (A) a resin component obtained by reacting an epoxy resin, an amino compound and/or a phenolic compound; (B) a resin component having a specific structural unit; (C) a blocked polyisocyanate compound; and (D) at least one rust inhibiting component selected from the group consisting of metal ions selected from zirconium, titanium, cobalt, vanadium, tungsten and molybdenum, oxymetal ions of the metal, and fluorometal ions of the metal.

Abstract: A multi-layer electrodeposition coating film-forming method which comprises subjecting a cationic electrodeposition coating composition containing at least two emulsions to an electrodeposition coating, said cationic electrodeposition coating composition being such that a difference in an electrical quantity (a) required for deposition starting between a first coating composition comprising a first emulsion and a second coating composition comprising a second emulsion in two emulsions selected from the at least two emulsions is in the range of 50 to 400 C/m2.

Abstract: The present invention provides a plastic-coated metal plate for an automobile exterior plate which is a laminate metal plate coated on both faces or one face of the metal plate with a plastic layer, wherein the plastic layer has a surface tension of at least 30 mN/m, an elongation percentage of at least 30% at a tensile rate of 20 mm/minute/20° C. and a rupture strength of at least 600 kg/cm2 at a tensile rate of 20 mm/minute/20° C., and a part for a major external face side in a car body, wherein the above plastic-coated metal plate is cut, molded and joined to form the part for a major external face side in a car body, and a metal-exposed part thereof is coated by electrodeposition.

Abstract: The present invention provides a plastics-covered metal plate excellent in chipping resistance, corrosion resistance etc. made by covering one surface or both surfaces of a metal plate with at least two kinds of plastics layers whose rates of elongation are different and a process of covering a car body by using said covered metal plate.

Abstract: According to the present invention, provided is a coated metal plate characterized by comprising a metal plate and laminated at least on one surface of a metal plate, a conductive plastic coated film and an electrodeposition coated film, which is useful as an outer plate part for car bodies and electrical appliances.

Abstract: A cationic coating composition containing (A) an unsaturated group-modified blocked polyisocyanate crosslinking agent obtained by reacting a hydroxyl group-containing unsaturated compound (a), a blocking agent (b) and a polyisocyanate compound (c), (B) a cationic epoxy resin, and (C) a photopolymerization initiator, preferably further containing a polymerizable unsaturated group-containing compound (D).

Abstract: The present invention relates to parts for car body comprising plastic-covered metallic material prepared by sticking a plastic film having a topcoat finishing property on one side or both sides of a molded and electrodeposition coated metallic material and to a coat-finishing process of a car body by using said parts for car body.

Abstract: The present invention provides a plastics-covered metal plate excellent in chipping resistance, corrosion resistance etc. made by covering one surface or both surfaces of a metal plate with at least two kinds of plastics layers whose rates of elongation are different and a process of covering a car body by using said covered metal plate.

Abstract: A cationic coating composition containing (A) an unsaturated group-modified cationic epoxy resin, (B) a blocked polyisocyanate crosslinking agent, and (C) a photopolymerization initiator, preferably further containing a polymerizable unsaturated group-containing compound (D).

Abstract: A multi-layer electrodeposition coating film-forming method which comprises subjecting a cationic electrodeposition coating composition containing at least two emulsions to an electrodeposition coating, said cationic electrodeposition coating composition being such that a difference in an electrical quantity (a) required for deposition starting between a first coating composition comprising a first emulsion and a second coating composition comprising a second emulsion in two emulsions selected from the at least two emulsions is in the range of 50 to 400 C/m2.

Abstract: The present invention provides a plastic-coated metal plate prepared by sticking a plastic layer on one face or both faces of a metal plate via a coating film of a thermosetting adhesive comprising an amine-added epoxy resin (A) and a polyisocyanate compound (B), which is excellent in a corrosion resistance, an adhesive property and a finishing property and which is particularly useful for forming a car body.

Abstract: This invention relates to cationic electro-coating composition which comprises blending which an aqueous dispersion or an aqueous dispersion paste which contains an organic acid-modified bismuth compound in a non-water-soluble state, and which is obtained by mixing and grinding a bismuth compound and an organic acid in an aqueous medium. Said cationic electro-coating composition, although containing no lead compounds, is capable of forming an electrocoated film which is excellent in corrosion resistance, appearance, etc.

Abstract: The present invention provides a method for forming a multilayer coating film, comprising: applying a colored cationic electrodeposition coating composition (A) to a metal substrate by electrodeposition; applying a bright pigment-containing clear coating composition (B) to the electrodeposition coating, which is either uncured or thermally cured; and then curing the uncured electrodeposition coating and the clear coating, or the clear coating.

Abstract: According to the present invention, provided is a coated metal plate characterized by comprising a metal plate and laminated at least on one surface of a metal plate, a conductive plastic coated film and an electrodeposition coated film, which is useful as an outer plate part for car bodies and electrical appliances.

Abstract: The present invention provides a plastic-coated metal plate for an automobile exterior plate which is a laminate metal plate coated on both faces or one face of the metal plate with a plastic layer, wherein the plastic layer has a surface tension of at least 30 mN/m, an elongation percentage of at least 30% at a tensile rate of 20 mm/minute/20° C. and a rupture strength of at least 600 kg/cm2 at a tensile rate of 20 mm/minute/20° C., and a part for a major external face side in a car body, wherein the above plastic-coated metal plate is cut, molded and joined to form the part for a major external face side in a car body, and a metal-exposed part thereof is coated by electrodeposition.

Abstract: The present invention provides a plastic-coated metal plate for an automobile exterior plate which is a laminate metal plate coated on both faces or one face of the metal plate with a plastic layer, wherein the plastic layer has a surface tension of at least 30 mN/m, an elongation percentage of at least 30% at a tensile rate of 20 mm/minute/20° C. and a rupture strength of at least 600 kg/cm2 at a tensile rate of 20 mm/minute/20° C., and a part for a major external face side in a car body, wherein the above plastic-coated metal plate is cut, molded and joined to form the part for a major external face side in a car body, and a metal-exposed part thereof is coated by electrodeposition.

Abstract: This invention provides a car body coating process wherein the metal-exposed portion of a shell body, a part or whole of which has been made of plastics-covered metal plates, is electrocoated with use of an electrodeposition paint which contains no coloring pigment and has a bath solid content of at most 10% by weight and which is capable of forming a clear coating film.