Abstract: The embodiments relate to a polyester film, which has a high tensile strength in the transverse direction and a low tensile strength in the longitudinal direction, while satisfying the condition of 0.5<A<6, A being calculated by Equation 1. A polyester film according to the embodiments can easily be cut in the transverse direction.

Abstract: The embodiments relate to a polyester film, which has a high tensile strength in the transverse direction and a low tensile strength in the longitudinal direction, while satisfying the condition of 0.5<A<6, A being calculated by Equation 1. A polyester film according to the embodiments can easily be cut in the transverse direction.

Abstract: A heat-shrinkable polyester film having a thermal shrinkage ratio of 15% or more in the longitudinal direction when treated at 100° C. for 10 seconds, a tensile strength at rupture in the longitudinal direction of 7 kgf/mm2 or more, and a difference between elongations at the hardening and yield points in the longitudinal direction of 15% or more exhibits superior properties, such as high tensile strength and crack-resistance in the longitudinal direction, suitable for labeling or shrink-wrapping containers.

Abstract: A multi-layer polymer film for printing and copying of the present invention comprising a two-layer polymer base film composed of layer A and layer B laminated on one side of the layer A, the layer B containing a filler in an amount of 50 to 3000 ppm and the layer A containing no filler or a filler in an amount of at least 1000 ppm and less than the B layer; an image receiving layer coated on the exposed surface of the layer A; and an antistatic layer coated on the exposed surface of the layer B, wherein the layer A having the image receiving coating layer and the layer B having the antistatic coating layer have average degrees of surface roughness (Ra) ranging from 10 to 60 nm and 50 to 150 nm, respectively, exhibits improved properties in terms of runnability, printing, optical (haze), antistatic, friction coefficient and anti-blocking properties, which can be advantageously used as an OHP film.

Abstract: A heat-shrinkable polyester film having a thermal shrinkage ratio of 15% or more in the longitudinal direction when treated at 100° C. for 10 seconds, a tensile strength at rupture in the longitudinal direction of 7 kgf/mm2 or more, and a difference between elongations at the hardening and yield points in the longitudinal direction of 15% or more exhibits superior properties, such as high tensile strength and crack-resistance in the longitudinal direction, suitable for labeling or shrink-wrapping containers.

Abstract: A multi-layer polymer film for printing and copying of the present invention comprising a two-layer polymer base film composed of layer A and layer B laminated on one side of the layer A, the layer B containing a filler in an amount of 50 to 3000 ppm and the layer A containing no filler or a filler in an amount of at least 1000 ppm and less than the B layer; an image receiving layer coated on the exposed surface of the layer A; and an antistatic layer coated on the exposed surface of the layer B, wherein the layer A having the image receiving coating layer and the layer B having the antistatic coating layer have average degrees of surface roughness (Ra) ranging from 10 to 60 nm and 50 to 150 nm, respectively, exhibits improved properties in terms of runnability, printing, optical (haze), antistatic, friction coefficient and anti-blocking properties, which can be advantageously used as an OHP film.