Abstract: Provided is a polishing composition which contains a water-soluble polymer and is suitable for reducing LPDs. The polishing composition provided in this application includes an abrasive, a water-soluble polymer, and a basic compound. In the polishing composition, the content of a reaction product of a polymerization initiator and a polymerization inhibitor is 0.1 ppb or less of the polishing composition on a weight basis.

Abstract: A power transmission belt is at least partially formed of a rubber composition. The rubber composition contains a rubber component, cellulose nanofibers, and carbon black. The amount of the cellulose nanofibers to be added is from 0.1 parts by mass to 20 parts by mass, relative to 100 parts by mass of the rubber component. The amount of the carbon black to be added is from 5 parts by mass to 80 parts by mass, relative to 100 parts by mass of the rubber component. The sum of the amount of the carbon black to be added and three times the amount of the cellulose nanofibers to be added is from 15 to 90.

Abstract: A power transmission belt at least includes a bottom rubber layer. A rubber composition for forming the bottom rubber layer contains a rubber component, cellulose fine fibers, and short fibers. The cellulose fine fibers have an average diameter from 1 nm to 200 nm, and the rubber composition contains 0.5 parts by mass or more of the cellulose fine fibers relative to 100 parts by mass of the rubber component. The short fibers have an average diameter from 5 ?m to 30 ?m, and the rubber composition contains 1 part by mass or more of the short fibers relative to 100 parts by mass the rubber component.

Abstract: Disclosed is a power transmission belt having a belt body made of rubber, and a cord embedded in the belt body so as to form a helical pattern having a pitch in a belt width direction. The cord is coated with an adhesion layer formed by an adhesion treatment and containing a rubber component, and the adhesion layer is in contact with a rubber composition containing cellulose-based fine fibers.

Abstract: A power transmission belt at least includes a bottom rubber layer. A rubber composition for forming the bottom rubber layer contains a rubber component, cellulose fine fibers, and short fibers. The cellulose fine fibers have an average diameter from 1 nm to 200 nm, and the rubber composition contains 0.5 parts by mass or more of the cellulose fine fibers relative to 100 parts by mass of the rubber component. The short fibers have an average diameter from 5 ?m to 30 ?m, and the rubber composition contains 1 part by mass or more of the short fibers relative to 100 parts by mass the rubber component.

Abstract: A power transmission belt is at least partially formed of a rubber composition. The rubber composition contains a rubber component, cellulose nanofibers, and carbon black. The amount of the cellulose nanofibers to be added is from 0.1 parts by mass to 20 parts by mass, relative to 100 parts by mass of the rubber component. The amount of the carbon black to be added is from 5 parts by mass to 80 parts by mass, relative to 100 parts by mass of the rubber component. The sum of the amount of the carbon black to be added and three times the amount of the cellulose nanofibers to be added is from 15 to 90.

Abstract: Disclosed is a power transmission belt having a belt body made of rubber, and a cord embedded in the belt body so as to form a helical pattern having a pitch in a belt width direction. The cord is coated with an adhesion layer formed by an adhesion treatment and containing a rubber component, and the adhesion layer is in contact with a rubber composition containing cellulose-based fine fibers.