Abstract: A stabilizer bushing installed on a stabilizer bar is made of two divided parts of rubber or the like to prevent or decrease generation of a gap in a bonding surface. The stabilizer bushing installed on an outer periphery of the stabilizer bar by adhesion includes divided rubber bushings of an upper rubber bushing and a lower rubber bushing. Before adhesion, both end portions of the upper and lower rubber bushings, respectively, in a circumferential direction are tapered so that an overlapping amount between the upper and lower rubber bushings increases toward the outer periphery side of the bushings. After adhesion, a bonding surface is bonded by pressure.

Abstract: A stabilizer bushing installed on a stabilizer bar is made of two divided parts of rubber or the like to prevent or decrease generation of a gap in a bonding surface. The stabilizer bushing installed on an outer periphery of the stabilizer bar by adhesion includes divided rubber bushings of an upper rubber bushing and a lower rubber bushing. Before adhesion, both end portions of the upper and lower rubber bushings, respectively, in a circumferential direction are tapered so that an overlapping amount between the upper and lower rubber bushings increases toward the outer periphery side of the bushings.

Abstract: A high-strength oil-tempered steel wire with excellent spring fabrication property that is made of spring low-alloy steel, having a decarburized layer of reduced hardness extending to a depth of not greater than 200 .mu.m from the wire surface, a wire surface hardness in the range from an Hv (Vickers hardness) of 420 to an Hv of 50 below the Hv of the wire interior, and an Hv at the interior of the wire beyond the depth of the decarburized layer of not less than 550. The spring low-alloy steel can preferably comprise, in weight percent, 0.45-0.80% C, 1.2-2.5% Si, 0.5-1.5% Mn, 0.5-2.0% Cr and the balance of Fe and unavoidable impurities.

Abstract: In a manufacturing method of a valve spring, a coiled valve spring made of an oil-tempered wire is applied with nitriding treatment and is supported to be rotated about its center axis. During a shot peening process of the coiled valve spring, cut wires of Hv 650 to 850 in hardness and 1.0 to 0.6 mm in diameter are shot to the coiled valve spring at a first step, in a roller-type shot machine and cut wires of Hv 650 to 850 in hardness and 0.4 to 0.2 mm in diameter are shot to the coiled valve spring at a second step in a tumbling shot machine, the time for the second step being longer than the time for the first step.

Abstract: A coil spring made of an oil-tempered steel wire with internal hardness of more than Hv 550 in cross-section, the surface hardness of the oil-tempered steel wire being determined in an extent between Hv 420 in a minimum value and hardness defined by subtraction of Hv 50 from the internal hardness in a maximum value.

Abstract: The present invention provides, at low cost, a valve spring steel having a tensile strength as high as 210 to 240 kgf/mm.sup.2 after oil tempering. The high strength spring steel comprises, based on weight, 0.65 to 0.85% of C, 1.90 to 2.40% of Si, 0.50 to 1.00% of Mn, 0.70 to 1.30% of Cr, 0.10 to 0.30% of Mo, 0.20 to 0.50% of V, 0.01 to 0.04% of Nb and the balance Fe and unavoidable impurities and is subjected to heating at temperature of 1,050 to 1,250.degree. C. and then to rolling so that carbides in the steel have a size of up to 0.15 .mu.m in terms of equivalent circle. A valve spring having a tensile strength as high as 210 to 240 kgf/mm.sup.2 after oil tempering and stabilized quality can be produced while the material cost is greatly reduced by decreasing costly alloying components as much as possible.