Abstract: An aluminum alloy conductive member for a transport instrument includes: a substrate formed of an aluminum alloy; and a metal oxide coating film that is formed on a surface of the substrate and that includes a metal oxide of an element other than Al. In the aluminum alloy conductive member, the total coating film amount of the metal oxide coating film is 0.1 to 40 mg/m2 in terms of metal equivalent mass, and a constituent of the metal oxide coating film includes an oxide of one or more selected from the element group X consisting of Ti, Zr, Hf, V, Nb, Ta, Mo, and W, and an oxide of one or more selected from the element group Y consisting of Zn, In, Mg, Sn, and Ca.

Abstract: Provided are: an Al—Mg—Si-based aluminum alloy material including an aluminum alloy including 0.10 to 1.50 mass % (hereinafter, “%”) Si and 0.10 to 2.00% of Mg, in which an oxide coating film mainly containing aluminum is formed on a surface of the aluminum alloy material, a Mg—Si-based crystallized product having an equivalent circle diameter of 0.1 to 5.0 ?m is contained at 100 to 150,000 particles/mm2, a Mg—Si-based crystallized product having an equivalent circle diameter of more than 5.0 ?m and 10.0 ?m or less is contained at 5 particles/mm2 or less, and the oxide coating film includes Si at a maximum concentration of 0.1 to 40.0% and Mg at a maximum concentration of 0.1 to 20.0%; a method for producing the aluminum alloy material; and an aluminum alloy clad material, in which the aluminum alloy material is clad on at least one surface of an aluminum core material.

Abstract: Provided are an aluminum cladding material having excellent corrosion resistance, a production method therefor, an aluminum cladding material for heat exchangers having excellent corrosion resistance, a production method therefor, an aluminum heat exchanger using said aluminum cladding material for heat exchangers, and a production method therefor. Said aluminum cladding material comprises an aluminum alloy core material and a sacrificial anode material layer clad on at least one surface thereof. The sacrificial anode material layer comprises an aluminum alloy containing 0.10 mass % or more and less than 1.50 mass % Si, 0.10 to 2.00 mass % Mg. Present therein is 100 to 150000 pieces/mm2 of Mg—Si-based crystallized product having a circle-equivalent diameter of 0.1 to 5.0 ?m, 7 pieces/mm2 or less of Mg—Si-based crystallized product having a circle-equivalent diameter of more than 5.0 ?m and 10.0 ?m or less in the sacrificial anode material layer.