Abstract: Provided is a crosslinked polyolefin foam is made by crosslinking and foaming the composition, wherein a product of 25% compressive strength (kPa) and tensile strength (MPa) of the crosslinked polyolefin foam at normal temperature is 35 to 65.

Abstract: Provided is a crosslinked polyolefin foam is made by crosslinking and foaming the composition, wherein a product of 25% compressive strength (kPa) and tensile strength (MPa) of the crosslinked polyolefin foam at normal temperature is 35 to 65.

Abstract: The crosslinked polyolefin resin foam of the present invention is a crosslinked polyolefin resin foam obtained by crosslinking and foaming a polyolefin resin composition comprising a polypropylene resin and an olefin rubber; the olefin rubber having a Mooney viscosity (ML1+4, 100° C.) of 15 to 85; the olefin rubber being contained in an amount of 10 to 150 parts by mass relative to 100 parts by mass of the polypropylene resin; the foam having a 25% compressive hardness of 30 to 70 kPa and a compressive strength ratio, 25% compressive strength/5% compressive strength, of 2.0 to 4.5. According to the present invention, a crosslinked polyolefin resin foam from which a molded product excellent in appearance can be obtained even in a secondary processing to a complicated shape without impairment of flexibility, and a molded product made from the same are provided.

Abstract: A crosslinked polyolefin foam that is a crosslinked foam of a polyolefin resin composition, the composition comprising a polyolefin resin (A) and a rubber (B) having a Mooney viscosity (ML1+4, 100° C.) of 15 to 85. The rubber (B) is contained in an amount of 10 to 150 parts by mass relative to 100 parts by mass of the polyolefin resin (A). The foam has a thickness of 1.5 mm or more, a 25% compressive hardness of 60 kPa or less, and a crosslinking degree of at least one of surface layers at both surfaces with a depth of 500 ?m from the surface that is at least 5% higher than the crosslinking degree of the middle layer excluding the both surface layers.

Abstract: The present invention relates to a foam having a density of 0.036 g/cc or more and less than 0.133 g/cc, having an elongation (%) at break at 160° C. of 150% or more as measured in accordance with JIS K6251, a value of 7 or more obtained by multiplying the elongation (%) at break by a 100% modulus (MPa) at 160° C. as measured in accordance with JIS K6251, and a cross-linking degree of 30 to 50%.

Abstract: The cross-linked polyolefin resin foam of the present invention is made by cross-linking and foaming a polyolefin resin composition comprising a polyolefin resin-containing resin (A), and a zeolite (B). The polyolefin resin composition includes 0.05 to 10 parts by mass of the zeolite (B) relative to 100 parts by mass of the resin (A) and the average particle diameter of the zeolite (B) is 0.1 to 30 ?m. According to the present invention, a cross-linked polyolefin resin foam capable of suppressing the generation of an odor without use of a coloring component such as carbon black can be provided, allowing the foam to be continuously produced using an extruder or the like with high productivity.

Abstract: The crosslinked polyolefin foam of the present invention is a crosslinked polyolefin foam made by crosslinking and foaming a polyolefin-based resin composition comprising a polypropylene-based resin and an elastomer, wherein the polypropylene-based resin being contained in an amount of 45 to 85 mass % based on the total resin components in the polyolefin-based resin composition, the crosslinked polyolefin foam having a 25% compressive strength of 60 to 120 kPa and a ratio of integral value of area under curve value of a stress-strain curve from 0% strain to 25% strain to a product of a strain of 25% and a stress at 25% strain of 0.45 to 0.65.

Abstract: The crosslinked polyolefin resin foam of the present invention is a crosslinked polyolefin resin foam obtained by crosslinking and foaming a polyolefin resin composition comprising a polypropylene resin and an olefin rubber; the olefin rubber having a Mooney viscosity (ML1+4, 100° C.) of 15 to 85; the olefin rubber being contained in an amount of 10 to 150 parts by mass relative to 100 parts by mass of the polypropylene resin; the foam having a 25% compressive hardness of 30 to 70 kPa and a compressive strength ratio, 25% compressive strength/5% compressive strength, of 2.0 to 4.5. According to the present invention, a crosslinked polyolefin resin foam from which a molded product excellent in appearance can be obtained even in a secondary processing to a complicated shape without impairment of flexibility, and a molded product made from the same are provided.

Abstract: The cross-linked polyolefin resin foam of the present invention is obtained by cross-linking and foaming a polyolefin resin composition, the composition including a polyolefin resin-containing resin (A), azodicarbonamide (B), and at least one basic magnesium (C) selected from the group consisting of magnesium oxide and magnesium hydroxide, wherein the amount of basic magnesium (C) included in the polyolefin resin composition is 0.05 to 0.5 parts by mass relative to 100 parts by mass of the resin (A), and the basic magnesium (C) has an average particle diameter of 0.1 to 15 ?m.

Abstract: A crosslinked polyolefin foam that is a crosslinked foam of a polyolefin resin composition, the composition comprising a polyolefin resin (A) and a rubber (B) having a Mooney viscosity (ML1+4, 100° C.) of 15 to 85. The rubber (B) is contained in an amount of 10 to 150 parts by mass relative to 100 parts by mass of the polyolefin resin (A). The foam has a thickness of 1.5 mm or more, a 25% compressive hardness of 60 kPa or less, and a crosslinking degree of at least one of surface layers at both surfaces with a depth of 500 ?m from the surface that is at least 5% higher than the crosslinking degree of the middle layer excluding the both surface layers.

Abstract: The present invention relates to a foam having a density of 0.036 g/cc or more and less than 0.133 g/cc, having an elongation (%) at break at 160° C. of 150% or more as measured in accordance with JIS K6251, a value of 7 or more obtained by multiplying the elongation (%) at break by a 100% modulus (MPa) at 160° C. as measured in accordance with JIS K6251, and a cross-linking degree of 30 to 50%.

Abstract: The present invention provides a stretched thermoplastic resin foam sheet that has excellent flexibility even compressed to a thickness as thin as about 0.05 mm, and a method for producing the same. The stretched thermoplastic resin foam sheet of the present invention is producible by stretching a thermoplastic resin foam sheet and has a compressive strength of 1 to 500 kPa as measured in accordance with JIS K6767 when compressed in a thickness direction thereof to a thickness of 0.05 mm. Accordingly, the stretched thermoplastic resin foam sheet has excellent flexibility even compressed to a thickness as thin as about 0.05 mm and is suitably used as a sealing material for a small electronic device such as mobile phones.

Abstract: The present invention provides a stretched thermoplastic resin foam sheet that has excellent flexibility even compressed to a thickness as thin as about 0.05 mm, and a method for producing the same. The stretched thermoplastic resin foam sheet of the present invention is producible by stretching a thermoplastic resin foam sheet and has a compressive strength of 1 to 500 kPa as measured in accordance with JIS K6767 when compressed in a thickness direction thereof to a thickness of 0.05 mm. Accordingly, the stretched thermoplastic resin foam sheet has excellent flexibility even compressed to a thickness as thin as about 0.05 mm and is suitably used as a sealing material for a small electronic device such as mobile phones.