Abstract: A method for producing a molded article of expanded beads includes filling tubular polypropylene-based resin expanded beads each having a through-hole in a mold, and supplying a heating medium to fusion-bond the expanded beads to each other. The expanded beads have a foamed layer constituted by polypropylene-based resin. A closed cell of the expanded beads is 90% or more. An average hole diameter (d) of through-holes of the expanded beads is less than 1 mm. A ratio [d/D] of the average hole diameter (d) to an average outer diameter (D) of the expanded beads is 0.4 or less. An open cell content of the molded article of expanded beads is 2.5% or more and 12% or less.

Abstract: A thermoplastic resin expanded bead and a molded article composed of the thermoplastic resin expanded beads are provided. The expanded bead includes a foam layer containing a thermoplastic resin. The expanded bead has a columnar shape, and has two or more and eight or less through-holes penetrating in the axial direction thereof. A ratio Ct/A of a total cross-sectional area Ct of the through-holes to a cross-sectional area A of the expanded bead in a cut surface obtained by cutting the expanded bead along a plane perpendicular to the axial direction at the center in the axial direction is 0.02 or more and 0.15 or less.

Abstract: A molded article of polyolefin-based resin expanded beads having excellent appearance and further suppressed color unevenness is provided. Polyolefin-based resin expanded beads obtained by expanding polyolefin-based resin particles including one or two or more metal borates selected from zinc borate and magnesium borate, wherein the particles of the metal borate has an arithmetic average particle diameter based on the number of 1 ?m or more, and a number rate of the particles of the metal borate having a particle diameter of 5 ?m or more is 20% or less.

Abstract: An expanded bead having a tubular shape with a through hole and a method for producing the same are provided. The expanded bead includes a foamed core layer and a covering layer. A polyolefin-based resin included in the covering layer has a melting point lower than a melting point of a polypropylene-based resin included in the foamed core layer. An average hole diameter d of the through hole of the expanded bead is less than 1 mm, and a ratio d/D of the average hole diameter d to an average outer diameter D of the expanded bead is 0.4 or less. The polypropylene-based resin for the foamed core layer has a flexural modulus of 1,200 MPa or more and a melting point of 158° C. or lower.