Abstract: A titanium alloy foil, wherein when a thickness is represented by t, the t is 0.005 mm or more and 0.200 mm or less, in X-ray diffraction intensities obtained when X-ray diffraction is performed on a surface, a peak intensity of a 200 plane of a crystal of a body-centered cubic structure is 5.0 times or larger a maximum peak intensity from other crystal structures, in X-ray diffraction intensities of the crystal of the body-centered cubic structure among the X-ray diffraction intensities, the peak intensity of the 200 plane or a peak intensity of a 211 plane is larger than a peak intensity of a 110 plane, and a tensile strength is 1,000 MPa or more and 1,800 MPa or less.

Abstract: Stainless steel foil with improved durability to repeated bending under the extreme bending conditions demanded of foldable displays and rollable displays. This stainless steel foil is flexible stainless steel foil comprising rolled stainless steel foil with a thickness of 0.1 mm or less, having a tensile strength of 1,800 MPa or more, and having a maximum height roughness of Rz of 0.35 ?m or less obtained from a roughness curve of the stainless steel foil surface as measured in the same direction as a tensile direction.

Abstract: An austenitic stainless steel foil according to this disclosure consists of, in mass %, C: 0.150% or less, Si: 1.00% or less, Mn: 2.00% or less, P: 0.045% or less, S: 0.0300% or less, Cr: 16.00 to 20.00%, Ni: 6.00 to 10.50%, N: 0.100% or less, Mo: 0 to 2.50%, Nb: 0 to 0.12%, V: 0 to 1.00%, Ta: 0 to 0.50%, Hf: 0 to 0.10%, Co: 0 to 0.50%, B: 0 to 0.0100%, Ca: 0 to 0.0200%, Mg: 0 to 0.0200%, rare earth metal: 0 to 0.0100%, Al: 0 to 0.010%, Ti: 0 to 0.500%, Zr: 0 to 0.100%, and Cu: 0 to 3.00%, with the balance being Fe and impurities. In an X-ray diffraction profile obtained using CuK? radiation, a full width at half maximum Fw of a peak of a {111} plane is greater than 0.366°.