Abstract: A biaxially-oriented film comprising a polyethylene having (A) a melt flow index of 1.0 g/10 min or more, (B) a density of 0.90 g/cm3 to less than 0.940 g/cm3, (C) a g?LCB of greater than 0.8, (D) ratio of comonomer content at Mz to comonomer content at Mw is greater than 1.0, (E) ratio of comonomer content at Mn to comonomer content at Mw is greater than 1.0, and (F) a ratio of the g?LCB to the g?zave is greater than 1.0, and where the film has a 1% secant in the transverse direction of 70,000 psi or more and Dart Drop of 350 g/mil or more.

Abstract: This invention relates to an oriented polyethylene film comprising polyethylene having: (A) a melt flow index of 1.0 g/10 min or more, (B) a density of 0.90 g/cm3 to less than 0.940 g/cm3, (C) a g?LCB of greater than 0.8, (D) ratio of comonomer content at Mz to comonomer content at Mw is greater than 1.0, (E) ratio of comonomer content at Mn to comonomer content at Mw is greater than 1.0, and (F) a ratio of the g?LCB to the g?Zave is greater than 1.0, where the film has a 1% secant in the transverse direction of 70,000 psi or more and Dart Drop of 350 g/mil or more.

Abstract: A thermoplastic vulcanizate comprises an isotactic polypropylene matrix phase in which cross-linked rubber particles are dispersed, the rubber particles comprising an ethylene-propylene-diene terpolymer (EPDM) containing at least 40 wt % of ethylene-derived units. A propylene-ethylene-diene terpolymer (PEDM) containing at least 60 wt % propylene-derived units and less than or equal to 25 wt % of ethylene-derived units and having a heat of fusion (Hf) of 2 to 10 J/g is added to compatibilize the propylene/EPDM blend.

Abstract: This invention relates to a method for forming a film including extruding the film from a polymer melt comprising a first polyolefin and 0.1 wt % to 30 wt % of a second polyolefin, wherein the second polyolefin has a density of at least 0.04 g/cm3 greater than a density of the first polyolefin, wherein a melt flow index of the first polyolefin is within 25% of a melt flow index of the second polyolefin, and wherein a polymer blend consisting of the first and second polyolefins in the same relative amounts as in the film has a multimodal differential scanning calorimetry melting profile above 40° C.; and stretching the film while the film is at a temperature above 25° C. and below the melting point of the second polyolefin to form elongated polyolefin structures in-situ in the film.

Abstract: This invention relates to blend, and films thereof, comprising: 1) semicrystalline cyclic olefin copolymer comprising less than 15 wt % of a C5-C40 cyclic olefin comonomer and greater than 85 wt % of a C2-C40 linear and/or branched olefin monomer content having a density of about 0.92 g/cm3 to about 0.94 g/cm3, modulus less than 20-80 kpsi, an elongation at break of 150-500%, and a glass transition temperatures less than 38° C.; 2) an amorphous cyclic olefin copolymer comprising more than 25 wt % of a C5-C40 cyclic olefin comonomer and less than 75 wt % of a C2-C40 linear and/or branched olefin monomer having a density greater than 1.0 g/cm3, a modulus of 260-380 kpsi, an elongation at break of <4%, and a glass transition temperature of 54 to 138° C.; and 3) a semicrystalline olefin copolymer comprising C2-C40 monomers having a density of about 0.90 g/cm3 to about 0.96 g/cm3, a modulus less than 150 kpsi, an elongation at break of greater than 400%, and a glass transition temperatures less than ?32° C.

Abstract: A thermoplastic vulcanizate comprises an isotactic polypropylene matrix phase in which cross-linked rubber particles are dispersed, the rubber particles comprising an ethylene-propylene-diene terpolymer (EPDM) containing at least 40 wt % of ethylene-derived units. A propylene-ethylene-diene terpolymer (PEDM) containing at least 60 wt % propylene-derived units and less than or equal to 25 wt % of ethylene-derived units and having a heat of fusion (Hf) of 2 to 10 J/g is added to compatibilize the propylene/EPDM blend.