Abstract: Provided are a barrier film having superior close adhesion to a phosphor layer when used for a wavelength conversion sheet, a wavelength conversion sheet having the barrier film, and a backlight and a display device including the wavelength conversion sheet. A barrier film for a wavelength conversion sheet, comprising: a barrier layer; and a primer layer, wherein the primer layer comprises a cured product of a polyurethane-based resin composition, and when a surface of an opposite side of the primer layer from the barrier layer is subjected to X-ray photoelectron spectroscopy to obtain a C1s spectrum, P2/P1 is 0.55 or more, where P1 is an area of a peak assigned to a C—C bond in the C1s spectrum and P2 is an area of a peak assigned to a C—O bond in the C1s spectrum.

Abstract: Provided is a method for surface-treating a metal component, whereby a pseudo-plated layer can be formed on a surface of a metal component, and quality equivalent to plating or other coating process can be obtained. The method includes a chemical polishing step scraping a surface of a base plate formed into a given shape through chemical polishing by 0.5 micrometer or more, and a heat treat pseudo-plating step forming a pseudo-plated layer on the surface through a heat treatment conducted by heating the base plate at a solution treatment temperature or above, for example, 850 degrees C. or above, preferably approximate 1040 degrees C., in a reducing atmosphere after the polishing step.

Abstract: Provided is a method for surface-treating a metal component, whereby a pseudo-plated layer can be formed on a surface of a metal component, and quality equivalent to plating or other coating process can be obtained. The method includes a chamical polishing step scraping a surface of a base plate formed into a given shape through chemical polishing by 0.5 micrometer or more, and a heat treat pseudo-plating step forming a pseudo-plated layer on the surface through a heat treatment conducted by heating the base plate at a solution treatment temperature or above, for example, 850 degrees C. or above, preferably approximate 1040 degrees C., in a reducing atmosphere after the polishing step.