Abstract: A process for forming a nanoporous silica dielectric coating on a substrate. A substrate containing a deposited film is suspended within a sealable hotplate, while remaining free of contact with the hotplate. The hotplate is sealed and an inert gas is flowed across the substrate. The hotplate is heated to a temperature of from about 350° C. or higher, and the substrate is forced to contact the heated hotplate. The substrate is heated for a time that sufficiently removes outgassing remnants from the resultant nanoporous dielectric coating.

Abstract: A process for forming a uniform nanoporous dielectric film on a substrate. The process includes horizontally positioning a flat substrate within a cup; depositing a liquid alkoxysilane composition onto the substrate surface; covering the cup such that the substrate is enclosed therein; spinning the covered cup and spreading the alkoxysilane composition evenly on the substrate surface; exposing the alkoxysilane composition to water vapor and base vapor to thereby form a gel; and then curing the gel. The invention also provides an apparatus for spin depositing a liquid coating onto a substrate. The apparatus has a cylindrical cup with an open top section and removable cover which closes the top. A vapor injection port extends through the center of the cover. Suitable means hold a substrate centered within the cup and spin the cup.

Abstract: A process for forming a uniform nanoporous dielectric film on a substrate. The process includes horizontally positioning a flat substrate within a cup; depositing a liquid alkoxysilane composition onto the substrate surface; covering the cup such that the substrate is enclosed therein; spinning the covered cup and spreading the alkoxysilane composition evenly on the substrate surface; exposing the alkoxysilane composition to water vapor and base vapor to thereby form a gel; and then curing the gel. The invention also provides an apparatus for spin depositing a liquid coating onto a substrate. The apparatus has a cylindrical cup with an open top section and removable cover which closes the top. A vapor injection port extends through the center of the cover. Suitable means hold a substrate centered within the cup and spin the cup.

Abstract: A process for forming a uniform nanoporous dielectric film on a substrate. The process includes horizontally positioning a flat substrate within a cup; depositing a liquid alkoxysilane composition onto the substrate surface; covering the cup such that the substrate is enclosed therein; spinning the covered cup and spreading the alkoxysilane composition evenly on the substrate surface; exposing the alkoxysilane composition to water vapor and base vapor to thereby form a gel; and then curing the gel. The invention also provides an apparatus for spin depositing a liquid coating onto a substrate. The apparatus has a cylindrical cup with an open top section and removable cover which closes the top. A vapor injection port extends through the center of the cover. Suitable means hold a substrate centered within the cup and spin the cup.

Abstract: A surface-coated nanoporous silica dielectric film that is prepared by a process comprising the steps of forming a nanoporous silica dielectric coating on a substrate, and coating the formed nanoporous silica dielectric film with a coating composition comprising a polymer precursor, under conditions effective to form a strength-enhancing and/or hydrophobicity enhancing layer on the treated nanoporous silica dielectric film.

Abstract: A process for treating silica dielectric film on a substrate, which includes reacting a suitable hydrophilic silica film with an effective amount of a multifunctional surface modification agent. The film is present on a substrate and optionally has a pore structure with hydrophilic pore surfaces, and the reaction is conducted for a period of time sufficient for said surface modification agent to penetrate said pore structure and produce a treated silica film having a dielectric constant of about 3 or less, wherein the surface modification agent is hydrophobic and suitable for silylating or capping silanol moieties on such hydrophilic surfaces. Dielectric films and integrated circuits including such films are also disclosed.

Abstract: An apparatus and method for forming thin film aerogels on semiconductor substrates is disclosed. It has been found that in order to produce defect-free nanoporous dielectrics with a controllable high porosity, it is preferable to substantially limit evaporation and condensation of pore fluid in the wet gel thin film, e.g. during gelation, during aging, and at other points prior to obtaining a dried gel. The present invention simplifies the atmospheric control needed to prevent evaporation and condensation by restricting the atmosphere in contact with the wet gel thin film to an extremely small volume. In one embodiment, a substrate 26 is held between a substrate holder 36 and a parallel plate 22, such that a substantially sealed chamber 32 exists between substrate surface 28 and chamber surface 30. Preferably, the average clearance between surfaces 28 and 30 is less than 5 mm, or more preferably, less than 1 mm. Temperature control means 34 may optionally be used to control the temperature in chamber 32.

Abstract: A process for forming a nanoporous dielectric silica coating on a surface of a substrate. The process includes spin-depositing alkoxysilane composition onto a surface of a substrate; spin depositing a surface hydrophobizing agent or a solvent onto an edge portion of the substrate to thereby remove the alkoxysilane composition from that area; and then curing the alkoxysilane composition to form a nanoporous dielectric silica coating. In another embodiment, an alkoxysilane composition layer is deposited onto a surface of a substrate. Then a solvent for the alkoxysilane substantially removes a portion of the alkoxysilane layer on the edge portion of the surface. This results in a transfer or cascading of a quantity of the alkoxysilane from a region adjacent to the edge portion to form a relatively thinner layer of the alkoxysilane onto the edge portion of the substrate surface. Then the relatively thinner alkoxysilane layer is removed prior to curing the alkoxysilane.

Abstract: The invention relates to nanoporous dielectric films and to a process for their manufacture. Such films are useful in the production of integrated circuits. Such films are produced from a precursor of an alkoxysilane; a relatively low volatility solvent composition comprising a e C.sub.1 to C.sub.4 alkylether of a C.sub.1 to C.sub.4 alkylene glycol which is miscible in water and alkoxysilanes, having a hydroxyl concentration of 0.0084 mole/cm.sup.3 or less, a boiling point of about 175.degree. C. or more at atmospheric pressure and a weight average molecular weight of about 120 or more; a relatively high volatility solvent composition having a boiling point below that of the relatively low volatility solvent composition; optional water and an optional catalytic amount of an acid.

Abstract: The invention relates to nanoporous dielectric films and to a process for their manufacture. Such films are useful in the production of integrated circuits. Such films are produced from a precursor of an alkoxysilane; a relatively low volatility solvent composition comprising an ether of a C.sub.1 to C.sub.4 alkylene glycol which is miscible in water and alkoxysilanes, having a hydroxyl concentration of 0.021 mole/cm.sup.3 or less, a boiling point of about 175 .degree. C. or more at atmospheric pressure and a weight average molecular weight of about 100 or more; a relatively high volatility solvent composition having a boiling point below that of the relatively low volatility solvent composition; optional water and an optional catalytic amount of an acid.

Abstract: A process for forming a nanoporous dielectric coating on a substrate. The process follows the steps of blending an alkoxysilane with a solvent composition and optional water; depositing the mixture onto a substrate while evaporating at least a portion of the solvent composition; placing the substrate in a sealed chamber and evacuating the chamber to a pressure below atmospheric pressure; exposing the substrate to water vapor at a pressure below atmospheric pressure and then exposing the substrate to base vapor.

Abstract: An apparatus and method for forming thin film aerogels on semiconductor substrates is disclosed. It has been found that in order to produce defect.about.free nanoporous dielectrics with a controllable high porosity, it is preferable to substantially limit evaporation and condensation of pore fluid in the wet gel thin film, e.g. during gelation, during aging, and at other points prior to obtaining a dried gel. The present invention simplifies the atmospheric control needed to prevent evaporation and condensation by restricting the atmosphere in contact with the wet gel thin film to an extremely small volume. In one embodiment, a substrate 26 is held between a substrate holder 36 and a parallel plate 22, such that a substantially sealed chamber 32 exists between substrate surface 28 and chamber surface 30. Preferably, the average clearance between surfaces 28 and 30 is less than 5 mm, or more preferably, less than 1 mm.

Abstract: A process for forming a nanoporous dielectric coating on a substrate. The process includes either (i) combining a stream of an alkoxysilane composition with a stream of a base containing catalyst composition to form a combined composition stream; immediately depositing the combined composition stream onto a surface of a substrate and exposing the combined composition to water (in either order or simultaneously); and curing the combined composition; or (ii) combining a stream of an alkoxysilane composition with a stream of water to form a combined composition stream; immediately depositing the combined composition stream onto a surface of a substrate; and curing the combined composition.

Abstract: A process for the manufacture of nanoporous silica dielectric films by vapor deposition of silica precursors on a substrate. The process provides for vaporizing at least one alkoxysilane composition; depositing the vaporized alkoxysilane composition onto a substrate; exposing the deposited alkoxysilane composition to a water vapor, and either an acid or a base vapor; and drying the exposed alkoxysilane composition, thereby forming a relatively high porosity, low dielectric constant, silicon containing polymer composition on the substrate.

Abstract: This invention has enabled a new, simple thin film nanoporous dielectric fabrication method. In general, this invention uses glycerol, or another low volatility compound, as a solvent. This new method allows thin film aerogels/low density xerogels to be made without supercritical drying, freeze drying, or a surface modification step before drying. Thus, this invention allows production of nanoporous dielectrics at room temperature and atmospheric pressure, without a separate surface modification step. Although this new method allows fabrication of aerogels without substantial pore collapse during drying, there may be some permanent shrinkage during aging and/or drying. This invention allows controlled porosity thin film nanoporous aerogels to be deposited, gelled, aged, and dried without atmospheric controls.