Abstract: A synthetic polyisoprene latex emulsion has pre-vulcanization composition and post vulcanization composition. The pre-vulcanization composition comprises insoluble amorphous sulfur extracted with zinc dithiocarbamate catalyst at 20° C. to form sulfur chain and transported to interior of synthetic polyisoprene particle forming physical attachment of sulfur to active sites. The degree of pre-vulcanization is verified by expansion of cast and dried film of latex in toluene in 20 minutes by means of a swelling index test. The latex emulsion is vulcanized at 90° C. to 120° C. for 3 to 5 minutes. Post-vulcanization composition with accelerators crosslink between synthetic polyisoprene particles, uniformly curing both in the inter-particle and intra-particle regions to produce high cross link density, uniform distribution of double bonds with zinc segregation at the boundaries of original particles.