Abstract: Process for preparing a catalyst composition containing a modified crystalline aluminosilicate and a binder, wherein the catalyst composition comprises from 5 to 95% by weight of crystalline aluminosilicate as based on the total weight of the catalyst composition, the process being remarkable in that it comprises a step of steaming said crystalline aluminosilicate: at a temperature ranging from 100° C. to 380° C.

Abstract: A process for the isomerizing dehydration of a feedstock including a primary monoalcohol, alone or as a mixture, of formula R—CH2—OH, wherein R is a nonlinear alkyl radical of general formula CnH2n+1 where n is an integer between 3 and 20, the process taking place in the gas phase at a weighted average temperature between 275° C. and 400° C., at a pressure between 0.3 MPa and 1 MPa and at a WWH (weight per weight per hour) between 5 and 10 h?1, in the presence of a catalyst containing at least one silicic binder and at least one zeolite having at least one series of channels, the opening of which is defined by a ring of 8 oxygen atoms (8MR), process wherein vaporized feedstock entering the reactor has a weight content of water of from 4% to 35%.

Abstract: Process for preparing a catalyst composition containing a modified crystalline aluminosilicate and a binder, wherein the catalyst composition comprises from 5 to 95% by weight of crystalline aluminosilicate as based on the total weight of the catalyst composition, the process being remarkable in that it comprises a step of steaming said crystalline aluminosilicate: at a temperature ranging from 100° C. to 380° C.

Abstract: Process for preparing a catalyst composition containing a modified crystalline aluminosilicate and a binder, wherein the catalyst composition comprises from 5 to 95% by weight of crystalline aluminosilicate as based on the total weight of the catalyst composition, the process being remarkable in that it comprises a step of steaming said crystalline aluminosilicate: at a temperature ranging from 100° C. to 380° C.

Abstract: The invention relates to a process for dehydration of a mono-alcohol, or of a mixture of at least two mono-alcohols, having at least 2 carbon atoms and at most 7 carbon atoms into olefins having the same number of carbons, wherein the process uses a catalyst composition that comprises a modified crystalline aluminosilicate has an acidity between 350 and 500 ?mol/g that comprises, and further wherein the catalyst composition is obtained by a process comprising the steps of providing a crystalline aluminosilicate having a Si/Al framework molar ratio greater than 10; and steaming said crystalline aluminosilicate, or said shaped and/or calcined crystalline aluminosilicate at a temperature ranging from 100° C. to 380° C.; and under a gas phase atmosphere, without liquid, containing from 5 wt % to 100 wt % of steam; at a pressure ranging from 2 to 200 bars; at a partial pressure of H2O from 2 bars to 200 bars; and said steaming being performed during at least 30 min and up to 144 h.

Abstract: A process for the isomerizing dehydration of a feedstock including a primary monoalcohol, alone or as a mixture, of formula R—CH2—OH, wherein R is a nonlinear alkyl radical of general formula CnH2n+1 where n is an integer between 3 and 20, the process taking place in the gas phase at a weighted average temperature between 275° C. and 400° C., at a pressure between 0.3 MPa and 1 MPa and at a WWH (weight per weight per hour) between 5 and 10 h?1, in the presence of a catalyst containing at least one silicic binder and at least one zeolite having at least one series of channels, the opening of which is defined by a ring of 8 oxygen atoms (8MR), process wherein vaporized feedstock entering the reactor has a weight content of water of from 4% to 35%.

Abstract: The invention relates to a process for dehydration of a mono-alcohol, or of a mixture of at least two mono-alcohols, having at least 2 carbon atoms and at most 7 carbon atoms into olefins having the same number of carbons, wherein the process uses a catalyst composition that comprises a modified crystalline aluminosilicate has an acidity between 350 and 500 ?mol/g that comprises, and further wherein the catalyst composition is obtained by a process comprising the steps of providing a crystalline aluminosilicate having a Si/Al framework molar ratio greater than 10; and steaming said crystalline aluminosilicate, or said shaped and/or calcined crystalline aluminosilicate at a temperature ranging from 100° C. to 380° C.; and under a gas phase atmosphere, without liquid, containing from 5 wt % to 100 wt % of steam; at a pressure ranging from 2 to 200 bars; at a partial pressure of H2O from 2 bars to 200 bars; and said steaming being performed during at least 30 min and up to 144 h.

Abstract: Process for preparing a catalyst composition containing a modified crystalline aluminosilicate and a binder, wherein the catalyst composition comprises from 5 to 95% by weight of crystalline aluminosilicate as based on the total weight of the catalyst composition, the process being remarkable in that it comprises a step of steaming said crystalline aluminosilicate: at a temperature ranging from 100° C. to 380° C.