Abstract: An unshaped product including, as weight percentages, A) particles (a) of at least one refractory material other than a glass and a glass-ceramic, and the main constituent(s) of which are alumina and/or zirconia and/or silica and/or chromium oxide: B) 2% to 15% of particles (b) of a hot binder chosen from glass-ceramic particles, particles made of a glass, and the mixtures of these particles, a glass being a noncrystalline material exhibiting a glass transition temperature of less than 1100° C., the hot binder not being in the solid state at 1500° C., C) less than 2% of particles (c) of hydraulic cement, D) less than 7% of other constituents, the particles (a) and (b) being distributed, as weight percentages in the following way: fraction<0.5 ?m: ?1%, fraction<2 ?m: ?4%, fraction<10 ?m: ?13%, fraction<40 ?m: 25%-52%.

Abstract: An unshaped product including, as weight percentages, A) particles (a) of at least one refractory material other than a glass and a glass-ceramic, and the main constituent(s) of which are alumina and/or zirconia and/or silica and/or chromium oxide: B) 2% to 15% of particles (b) of a hot binder chosen from glass-ceramic particles, particles made of a glass, and the mixtures of these particles, a glass being a noncrystalline material exhibiting a glass transition temperature of less than 1100° C., the hot binder not being in the solid state at 1500° C., C) less than 2% of particles (c) of hydraulic cement, D) less than 7% of other constituents, the combined particles (a) and (b) being distributed, as weight percentages in the following way: fraction <0.5 ?m: ?1%, fraction <2 ?m: ?4%, fraction <10 ?m: ?13%, fraction <40 ?m: 25%-52%.

Abstract: A powder including, in percentages by weight: (a) 94% to 99% of particles of at least one refractory material, the main constituent(s) of which are alumina and/or zirconia and/or silica; (b) 1% to 6% of a hydraulic cement; (c) 0 to 0.03% of organic fibers; (d) optionally, 0.075% to 1% of a surfactant; and (e) optionally, a setting accelerator, where the fraction of particles having a size below 40 ?m being distributed, in percentages by weight relative to the weight of the powder, in the following manner: (1) fraction<0.5 ?m: ?4%, (2) fraction<2 ?m: ?5%, fraction<10 ?m: ?16%, and fraction<40 ?m: 29-45%, where the proportion of zirconia in the fraction of particles having a size smaller than 10 ?m, called “fines”, is between 35% and 75% by weight relative to the total weight of said fraction.

Abstract: A powder including, in percentages by weight: (a) 94% to 99% of particles of at least one refractory material, the main constituent(s) of which are alumina and/or zirconia and/or silica; (b) 1% to 6% of a hydraulic cement; (c) 0 to 0.03% of organic fibres; (d) optionally, 0.075% to 1% of a surfactant; and (e) optionally, a setting accelerator, where the fraction of particles having a size below 40 ?m being distributed, in percentages by weight relative to the weight of the powder, in the following manner: (1) fraction<0.5 ?m:?4%, (2) fraction<2 ?m:?5%, fraction<10 ?m:?16%, and fraction<40 ?m:29-45%, where the proportion of zirconia in the fraction of particles having a size smaller than 10 ?m, called “fines”, is between 35% and 75% by weight relative to the total weight of said fraction.