Abstract: A process for the manufacture of maleated polypropylenes having an acid number greater than 6, a yellowness index color of no greater than 76, and a number average molecular weight of at least 20,000. The process for making the maleated polypropylenes includes forming a mixture of molten polypropylene and molten maleic anhydride in a reactor, introducing a free radical initiator into the molten mixture to produce a product having maleic anhydride grafted onto the polypropylene, and recovering a high acid number, high molecular weight maleated polypropylene of low color from the reactor.

Abstract: A process for the manufacture of maleated polypropylenes having an acid number greater than 6, a yellowness index color of no greater than 76, and a number average molecular weight of at least 20,000. The process for making the maleated polypropylenes includes forming a mixture of molten polypropylene and molten maleic anhydride in a reactor, introducing a free radical initiator into the molten mixture to produce a product having maleic anhydride grafted onto the polypropylene, and recovering a high acid number, high molecular weight maleated polypropylene of low color from the reactor.

Abstract: A process for the manufacture of maleated polypropylenes having an acid number greater than 4.5, a yellowness index color of no greater than 76, and a number average molecular weight of at least 20,000. The process for making the maleated polypropylenes includes forming a mixture of molten polypropylene and molten maleic anhydride in a reactor, introducing a free radical initiator into the molten mixture to produce a product having maleic anhydride grafted onto the polypropylene, and recovering a high acid number, high molecular weight maleated polypropylene of low color from the reactor.

Abstract: A novel, continuous process for the manufacture of novel higher molecular weight and higher acid numbered maleated polypropylenes with lower color at higher efficiencies involving specified ratios of polypropylene, maleic anhydride, and free radical initiator is described. The novel maleated polypropylenes have an acid number greater than 4.5, a yellowness index color of no greater than 76, and a number average molecular weight of at least 20,000. The process entails continuously forming an intimate mixture of molten polypropylene and molten maleic anhydride at one end of a reactor, continuously introducing a free radical initiator, and continuously removing high acid number high molecular weight maleated polypropylene of low color from the opposite end of the reactor.

Abstract: A novel, continuous process for the manufacture of novel higher molecular weight and higher acid numbered maleated polypropylenes with lower color at higher efficiencies involving specified ratios of polypropylene, maleic anhydride, and free radical initiator is described. The novel maleated polypropylenes have an acid number greater than 4.5, a yellowness index color of no greater than 76, and a number average molecular weight of at least 20,000. The process entails continuously forming an intimate mixture of molten polypropylene and molten maleic anhydride at one end of a reactor, continuously introducing a free radical initiator, and continuously removing high acid number high molecular weight maleated polypropylene of low color from the opposite end of the reactor.

Abstract: A novel, continuous process for the manufacture of novel higher molecular weight and higher acid numbered maleated polypropylenes with lower color at higher efficiencies involving specified ratios of polypropylene, maleic anhydride, and free radical initiator is described. The novel maleated polypropylenes have an acid number greater than 4.5, a yellowness index color of no greater than 76, and a number average molecular weight of at least 20,000. The process entails continuously forming an intimate mixture of molten polypropylene and molten maleic anhydride at one end of a reactor, continuously introducing a free radical initiator, and continuously removing high acid number high molecular weight maleated polypropylene of low color from the opposite end of the reactor.