Abstract: The invention relates to a single- or multilayer, oriented film in which at least one layer is comprised of a thermoplastic polymer having a minimum amount of amide groups. The polymer is a polyester, a polyamide, or a mixture comprised of polyester and polyamide, or is a copolymer comprised of these two materials. The film also comprises a component a) which, when irradiated with electromagnetic or particulate radiation, forms metal nuclei onto which further metal can be accumulated in further steps of the process. The invention also relates to a process for the production of this film, and to its use in printed circuit boards, ribbon cables, smart cards, RFID labels, membrane keyboards, or film-based circuits of any type.

Abstract: The invention relates to a single- or multilayer, biaxially oriented polyester film where at least one layer includes an amount of from 0.2 to <1.0 % by weight, based on the total weight of the film, of silicon dioxide particles whose median particle size, d50 is from 2.5 to 4.5 ?m. The inventive films have particular suitability in the industrial sector, e.g. for greenhouses, for more diffuse light-scattering.

Abstract: The invention relates to a hydrolysis-stable polyester whose thickness is preferably in the range from 0.4 to 500 ?m. The film comprises polyester and at least one hydrolysis stabilizer and is distinguished by its low hydrolysis rate. The invention furthermore relates to a process for the production of the film and its use.

Abstract: The invention relates to a hydrolysis-stable polyester film comprising a polyester, whose thickness is preferably in the range from 0.4 to 500 ?m. The film comprises polyester and at least one hydrolysis stabilizer and is distinguished by its low hydrolysis rate. The invention furthermore relates to a process for the production of the film and its use.

Abstract: Multilayer, biaxially oriented polyester films which include as a constituent of the base layer B, a crystallizable polyester with increased diethylehe glycol content and/or increased polyethylene glycol content, and/or increased isophthalic acid content, preferably polyethylene terephthalate. The outer layers of the inventive films advantageously include at least one IR-reflective pigment and one UV stabilizer. The inventive films advantageously feature adjustable mattness, diffuse scattering power for visible light, high light transmittance, IR reflectance, and good thermoformability, and are suitable for thermally protective coatings or thermally protective packaging.

Abstract: Biaxially oriented polyester films formed from a crystallizable polyester having increased diethylene glycol content and/or increased polyethylene glycol content, and/or increased isophthalic acid content, preferably polyethylene terephthalate. The films of the invention further include at least one IR-reflective pigment and one UV stabilizer. The inventive films feature adjustable mattness, diffuse scattering power for visible light, high light transmittance and IR reflectance and good thermoformability, and are suitable for thermally protective coatings or thermally protective packaging.

Abstract: The invention relates to a single- or multilayer, white, biaxially oriented polyester film. Films of the invention are formed from thermoplastic polyester and are coated on at least one side with a water-soluble adhesion-promoting layer that includes a hydrolyzed amino-functional silane. The invention further relates to the use of the film and to a process for its production.

Abstract: The invention relates to a transparent, electrically conductive, biaxially oriented, single- or multilayer polyester film which includes a coating composed of (a) conductive (ITO) indium tin oxide particles or (ATO) antimony tin oxide particles, or of a mixture of these. The film further include other conductive components (b). The other conductive components (b) may be present either in the coating including ITO particles and/or ATO particles or in a layer in contact therewith. The conductive component (b) may also be a metal layer in contact with the ITO and/or ATO. The film is only oriented or relaxed prior to application of the ITO and/or ATO coating. The invention further relates to a process for the production of the film, and its use.

Abstract: The invention relates to a single- or multilayer, oriented film in which at least one layer is comprised of a thermoplastic polymer having a minimum amount of amide groups. The polymer is a polyester, a polyamide, or a mixture comprised of polyester and polyamide, or is a copolymer comprised of these two materials. The film also comprises a component a) which, when irradiated with electromagnetic or particulate radiation, forms metal nuclei onto which further metal can be accumulated in further steps of the process. The invention also relates to a process for the production of this film, and to its use in printed circuit boards, ribbon cables, smart cards, RFID labels, membrane keyboards, or film-based circuits of any type.

Abstract: The invention relates to a single- or multilayer, oriented film comprised of a polyester which comprises an additive which when irradiated with electromagnetic radiation forms metal nuclei on which further metal can be accumulated in further steps of the process. The film also comprises another, radiation-absorbing material. The invention further relates to a process for the production of this film and to its use in printed circuit boards, ribbon cables, smart cards, RFID labels, membrane keyboards, and film-based circuits of any type.

Abstract: The invention relates to a single-layer, oriented polyester film where the polyester comprises an additive which on irradiation with electromagnetic radiation forms metal nuclei on which further metal can be accumulated during further steps of the process. The invention further relates to a process for producing this film and to its use in printed circuit boards, ribbon cables, smart cards, RFID labels, membrane keyboards, and film-based circuits, of any type.

Abstract: The invention relates to a multilayer, oriented film, in which at least one layer comprises a polyester which comprises an additive which, on irradiation with electromagnetic radiation, forms metal nuclei on which further metal can be deposited in further steps of the process. The invention further relates to a process for the production of this film and to its use in printed circuit boards, ribbon cables, smart cards, RFID labels, membrane keyboards, and film-based circuits of any type.

Abstract: The invention relates to a white, biaxially oriented film made from a crystallizable thermoplastic with high whiteness, the thickness of the film being in the range from 10 to 500 ?m. The film comprises at least one rutile-type titanium dioxide as pigment and an optical brightener, with or without other additives, and has at least one additional functionality. The expression “additional functionality” includes UV resistance, yellowing resistance, photooxidative stability, flame retardancy, and sealability. This film may have one or more of the functional properties. All of these films are capable of cost-effective thermoforming, have good orientability, and have very good optical and mechanical properties. The invention further relates to a process for its production.

Abstract: The invention relates to a single- or multilayer, oriented, film coated with an aminosilane compound and composed of polyester which comprises an additive which, on irradiation with electromagnetic radiation, forms metal nuclei on which further metal can be deposited in further steps of the process. The invention further relates to a process for producing this film and to its use in printed circuit boards, ribbon cables, smart cards, RFID labels, membrane keyboards, and film-based circuits of any type.

Abstract: The invention relates to transparent, biaxially oriented and heat-set films having one or more layers and compris, as main constituent, at least one crystallizable thermoplastic, in particular a polyester, and also comprise at least one hydrolysis stabilizer. The hydrolysis stabilizer is preferably a phenolic compound, an oxazoline, and/or a monomeric or polymeric carbodiimide, where appropriate combined with an organic phosphite. It is preferably added in the form of a masterbatch. The film exhibits low longitudinal and transverse shrinkage. On exposure to moisture and heat it shows practically no embrittlement and retains its ultimate tensile strength. The additional functionality is preferably that the film has been made UV-resistant, or flame-retardant, or on one side or on both sides has been coated, or is sealable, and/or has been corona- or flame-treated.

Abstract: White, biaxially oriented polyester films which have a base layer B which comprises a thermoplastic polyester such as polyethylene terephthalate, and which comprise substantially only TiO2 as a white pigment, whose R value is less than 43 daN/mm2, whose emax ratio is less than 2.5 and at least one of whose two surfaces of the film has been provided with an acrylate-containing coating, are particularly tear-resistant and do not tend to delamination and are therefore suitable in particular as lid films for food containers, for example yoghurt cups. A process is described for producing the films.

Abstract: The invention relates to a polyester film with a thickness of from about 4 to about 23 &mgr;m, which comprises, alongside polyethylene terephthalate as main constituent, from about 2 to about 20% by weight of polyethylene naphthalate (based on the weight of the film), and has fewer than 30 pinholes per 100 m2. The invention further relates to a process for producing these films, and to the use of the films in packaging composites.

Abstract: The invention relates to an at least two-layer polyester film with a total thickness of from 5 to 200 &mgr;m which comprises, alongside polyethylene terephthalate, from 2 to 20% by weight—based on the weight of the entire film—of polyethylene naphthalate (PEN), where at least one outer layer comprises less than 0.1% by weight of PEN (based on the weight of this outer layer).

Abstract: The invention relates to a biaxially oriented, hydrolysis-resistant film made from a thermoplastic and having a thickness in the range from 0.5 to 12 &mgr;m. The film comprises at least one hydrolysis stabilizer resistant to evolution of gases and has not only a low hydrolysis rate but also good dielectric properties, and in particular has high dielectric strength. The hydrolysis stabilizer has only low tendency to cause evolution of gases during heating of the film. The invention further relates to a process for producing this film and to the use of the film and also to capacitors produced from the film.

Abstract: The invention relates to a biaxially oriented, hydrolysis-resistant film comprising a crystallizable thermoplastic, with a thickness in the range from 0.5 to 12 &mgr;m. The film comprises at least one hydrolysis retardant, has a conductive coating and is notable for its low hydrolysis speed and its good dielectric properties. The film may possess at least one functionality additional to the hydrolysis resistance. In particular, it has a high tracking resistance and a low dissipation factor, and may also have one or more further functionalities. The invention additionally relates to a process for producing the film and to its use.