Abstract: The present disclosure provides a copper-phosphorus-tin brazing wire and a preparation method thereof, relates to the technical field of brazing materials. The copper-phosphorus-tin brazing wire is of a three-layer structure, the inner layer is Cu, the middle layer is Cu-14P alloy, and the outer layer is Sn, wherein the mass percentage of Sn is over 7%. The present disclosure solves the technical problems in the prior art that the copper-phosphorus-silver brazing filler metal is prone to produce defects such as pores and inclusions when brazing copper alloys, which leads to the decline of the mechanical properties of the joint, and simultaneously provides the preparation method of the copper-phosphorus-tin brazing wire, such that the technical problem that it is difficult to obtain copper-phosphorus-tin brazing wire with a wire diameter below 0.5 mm under the condition of high Sn content is solved.

Abstract: Copper-tin-nickel brazing material prepared by alloys recycled from E-waste, preparation method therefor, and system thereof are provided. A preparation method for the copper-tin-nickel brazing material includes the following steps: (a) spreading nano-SiO2 on the bottom of crucible and then adding a crude copper-tin-iron-nickel alloy recycled from E-waste; (b) heating the crucible to melt the crude alloy into a metal liquid so that Zn and Pb in the metal liquid react with the SiO2 to form a slag that floats out; (c) introducing a refining gas to the bottom of metal liquid in step (b), thereby removing the scums or gases formed by Pb, Fe, S, and O in the metal liquid; (d) performing heat-preserving directional solidification on the metal liquid, to bias-aggregate the Fe and Sb at one end and remove the same to obtain a copper-based intermediate alloy; and smelting and powdering the copper-based intermediate alloy.

Abstract: The present disclosure provides a copper-phosphorus-tin brazing wire and a preparation method thereof, relates to the technical field of brazing materials. The copper-phosphorus-tin brazing wire is of a three-layer structure, the inner layer is Cu, the middle layer is Cu-14P alloy, and the outer layer is Sn, wherein the mass percentage of Sn is over 7%. The present disclosure solves the technical problems in the prior art that the copper-phosphorus-silver brazing filler metal is prone to produce defects such as pores and inclusions when brazing copper alloys, which leads to the decline of the mechanical properties of the joint, and simultaneously provides the preparation method of the copper-phosphorus-tin brazing wire, such that the technical problem that it is difficult to obtain copper-phosphorus-tin brazing wire with a wire diameter below 0.5 mm under the condition of high Sn content is solved.