Abstract: Processes for preparing stabilized metal-containing nanoparticles comprising silver and/or a silver alloy composite by reacting a silver compound with a reducing agent comprising a hydrazine compound at a temperature between about 20° C. and about 60° C. The reaction being carried out by incrementally adding the silver compound or a mixture of the silver compound and a stabilizer to a solution comprising the reducing agent, a stabilizer, and a solvent. Conductive ink compositions containing stabilized metal-containing nanoparticles prepared by such processes.

Abstract: Processes for preparing stabilized metal-containing nanoparticles comprising silver and/or a silver alloy composite by reacting a silver compound with a reducing agent comprising a hydrazine compound at a temperature between about 20° C. and about 60° C. The reaction being carried out by incrementally adding the silver compound or a mixture of the silver compound and a stabilizer to a solution comprising the reducing agent, a stabilizer, and a solvent. Conductive ink compositions containing stabilized metal-containing nanoparticles prepared by such processes.

Abstract: Processes for preparing stabilized metal-containing nanoparticles comprising silver and/or a silver alloy composite by reacting a silver compound with a reducing agent comprising a hydrazine compound at a temperature between about 20° C. and about 60° C. The reaction being carried out by incrementally adding the silver compound or a mixture of the silver compound and a stabilizer to a solution comprising the reducing agent, a stabilizer, and a solvent. Conductive ink compositions containing stabilized metal-containing nanoparticles prepared by such processes.

Abstract: Methods for making amorphous resins for use in robust solid ink applications are disclosed in which an organic acid is reacted with an alcohol in the presence of a solvent in the amount of from about 0.5 to about 1.5 grams of solvent per gram of reaction product. The reaction product is an ester of tartaric acid or an ester of citric acid.

Abstract: In an embodiment, there is a method of preparing a conductive ink formulation. The method can include dissolving a stabilizer in a first solvent, adding a reducing agent to the first solvent, adding a metal salt to the first solvent and forming a slurry by precipitating stabilized metal nanoparticles in the first solvent. The method can also include forming a wet cake of the stabilized metal nanoparticles and adding the wet cake to a second solvent. The second solvent can include at least one of a polyvinyl alcohol derivative. The wet cake may not be actively dried prior to being added to the second solvent.

Abstract: In an embodiment, there is a method of preparing a conductive ink formulation. The method can include dissolving a stabilizer in a first solvent, adding a reducing agent to the first solvent, adding a metal salt to the first solvent and forming a slurry by precipitating stabilized metal nanoparticles in the first solvent. The method can also include forming a wet cake of the stabilized metal nanoparticles and adding the wet cake to a second solvent. The second solvent can include at least one of a polyvinyl alcohol derivative. The wet cake may not be actively dried prior to being added to the second solvent.

Abstract: Processes for preparing stabilized metal-containing nanoparticles comprising silver and/or a silver alloy composite by reacting a silver compound with a reducing agent comprising a hydrazine compound at a temperature between about 20° C. and about 60° C. The reaction being carried out by incrementally adding the silver compound or a mixture of the silver compound and a stabilizer to a solution comprising the reducing agent, a stabilizer, and a solvent. Conductive ink compositions containing stabilized metal-containing nanoparticles prepared by such processes.

Abstract: Methods for making amorphous resins for use in robust solid ink applications are disclosed in which an organic acid is reacted with an alcohol in the presence of a solvent in the amount of from about 0.5 to about 1.5 grams of solvent per gram of reaction product. The reaction product is an ester of tartaric acid or an ester of citric acid.