Abstract: A method is provided for forming an SOI MOSFET device with a silicon layer formed on a dielectric layer with a gate electrode stack, with sidewall spacers on sidewalls of the gate electrode stack and raised source/drain regions formed on the surface of the silicon layer. The gate electrode stack comprises a gate electrode formed of polysilicon over a gate dielectric layer formed on the surface of the silicon layer. A thin amorphous silicon cap layer is formed in the top surface of the gate electrode by implanting dopant into the surface thereof. A notch is etched into the periphery of the cap layer. A plug of dielectric material is formed in the notch. The sidewalls of the gate electrode are covered by the sidewall spacers which cover a portion of the plug for the purpose of eliminating the exposure of the gate polysilicon so that formation of spurious epitaxial growth during the formation of raised source/drain regions is avoided.

Abstract: A method for precise thinning to form a recess to a precise depth in a crystalline silicon layer, which can be used to form various devices, such as MOSFET devices, includes the following steps. Form a patterning mask with a window therethrough over the top surface of the silicon layer. Form an amorphized region in the top surface of the silicon layer below the window. Selectively etch away the amorphized region of the silicon layer to form a recess in the surface of the silicon layer, and remove the patterning mask. In the case of an MOSFET device form a hard mask below the patterning mask with the window extending therethrough. Then create sidewall spacers in the window through the hard mask and form a gate electrode stack in the window. Then remove the hard mask and form the source/drain extensions, halos and regions plus silicide and complete the MOSFET device.

Abstract: The present invention provides a method for forming an interconnect to a cobalt or nickel silicide having a TiN diffusion barrier. The inventive method comprises providing an initial structure having vias to exposed silicide regions positioned on a substrate; annealing the initial structure in a nitrogen-containing ambient, wherein a nitrogen passivation layer is formed atop the exposed silicide region; depositing Ti atop the nitrogen passivation layer; annealing the Ti in a nitrogen-containing ambient to form a TiN diffusion barrier and an amorphous Ti cobalt silicide between the TiN diffusion layer and the cobalt or nickel silicide and depositing an interconnect metal within the vias and atop the TiN diffusion barrier. The nitrogen passivation layer substantially restricts diffusion between the Ti and silicide layers minimizing the amorphous Ti cobalt silicide layer that forms. Therefore, the amorphous Ti cobalt or Ti nickel silicide is restricted to a thickness of less than about 3.0 nm.

Abstract: A method for precise thinning to form a recess to a precise depth in a crystalline silicon layer, which can be used to form various devices, such as MOSFET devices, includes the following steps. Form a patterning mask with a window therethrough over the top surface of the silicon layer. Form an amorphized region in the top surface of the silicon layer below the window. Selectively etch away the amorphized region of the silicon layer to form a recess in the surface of the silicon layer, and remove the patterning mask In the case of an MOSFET device form a hard mask below the patterning mask with the window extending therethrough. Then create sidewall spacers in the window through the hard mask and form a gate electrode stack in the window. Then remove the hard mask and form the source/drain extensions, halos and regions plus silicide and complete the MOSFET device.

Abstract: A method of fabricating a Ti-containing liner having good contact resistance and coverage of a contact hole is provided. The method which converts an amorphous region of ionized metal plasma deposited Ti into a substantially crystalline region includes (a) providing a structure having at least one contact hole formed therein, said at least one contact hole exposing at least a portion of a cobalt disilicide contact formed in a semiconductor substrate; (b) depositing a Ti/TiN liner in said at least one contact hole by ionized metal plasma deposition; (c) annealing said Ti/TiN liner under conditions effective to recrystallize any amorphous region formed during said annealing into a crystalline region including a TiSi2 top layer and a CoSix bottom layer; and (d) optionally forming a conductive material on said Ti/TiN liner.

Abstract: A dry etching process for etching an oxide layer on a substrate in which a plasma is created in a gaseous mixture containing C.sub.4 F.sub.8 and C.sub.2 F.sub.6. The dry etch process is useful for etching an oxide layer stopping on a silicon nitride layer on a semiconductor wafer of an integrated circuit structure as it eliminates resist blistering without sacrificing high selectivity to nitride, via wall angle, and/or etch uniformity.