Abstract: An antifouling condensation curing organopolysiloxane composition is prepared by premixing a part or all of (A) a diorganopolysiloxane free of a reactive group with a part or all of (B) silica to form a premix, then mixing the premix with the remainder of (A) and (B), (C) a base diorganopolysiloxane, and (D) a silane. The composition has a good balance of low viscosity and high thixotropy, can be thickly coated in a single pass, and cures into a coating having rubber strength and surface smoothness and exhibiting satisfactory antifouling property over a long period of time.

Abstract: A process for producing a room temperature vulcanizable organopolysiloxane composition comprising: (A) 100 parts by weight of a diorganopolysiloxane having in one molecule at least two hydroxyl groups and/or hydrolyzable groups connecting to silicon atoms; (B) 0.2 to 10 parts by weight of an alkylene oxide compound having silicon atoms in a molecule; (C) 0.5 to 100 parts by weight of a silica; and (D) 0.5 to 30 parts by weight of a silane and/or condensate of partial hydrolyzate thereof, wherein said process comprises steps of hot-mixing component (A), component (B), and component (C) together, and subsequently mixing component (D) thereto.

Abstract: A cleaning fluid comprising at least two components selected from organic acids, organic acid salts, electrolytes, alcohols, and water is safe. When the existing antifouling coating is to be overcoated or repaired, the surface of the existing coating is cleaned with the cleaning fluid so that a repair coating composition may strongly bond to the existing coating.

Abstract: A process for producing a room temperature vulcanizable organopolysiloxane composition comprising: (A) 100 parts by weight of a diorganopolysiloxane having in one molecule at least two hydroxyl groups and/or hydrolyzable groups connecting to silicon atoms; (B) 0.2 to 10 parts by weight of an alkylene oxide compound having silicon atoms in a molecule; (C) 0.5 to 100 parts by weight of a silica; and (D) 0.5 to 30 parts by weight of a silane and/or condensate of partial hydrolyzate thereof, wherein said process comprises steps of hot-mixing component (A), component (B), and component (C) together, and subsequently mixing component (D) thereto.

Abstract: An antifouling condensation curing organopolysiloxane composition is prepared by premixing a part or all of (A) a diorganopolysiloxane free of a reactive group with a part or all of (B) silica to form a premix, then mixing the premix with the remainder of (A) and (B), (C) a base diorganopolysiloxane, and (D) a silane. The composition has a good balance of low viscosity and high thixotropy, can be thickly coated in a single pass, and cures into a coating having rubber strength and surface smoothness and exhibiting satisfactory antifouling property over a long period of time.

Abstract: A new nitriding process by using a salt bath to produce iron and steel parts having excellent abrasion resistance and corrosion resistance includes forming an iron lithium complex oxide layer at the outermost surface of the iron part by immersing the iron and steel parts in a salt bath containing cationic component of Li, Na and K and anionic components of CNO?and CO32?, where hydroxide compound selected from lithium hydroxide, sodium hydroxide and potassium hydroxide are added to the salt bath. Materials being in a hydrated state or in a free water containing state can be used for preparation or replenishing of the salt bath. Moistened air of (1×10?2 kg·H2O)/(1 kg dry air) can be used for mixing the salt bath. Containing ratio of Li, Na, K is preferable where a solidifying temperature of the mixture of carbonates of Li, Na, K in that ratio is lower than 500° C.

Abstract: A new nitriding process by using a salt bath to produce iron and steel parts having excellent abrasion resistance and corrosion resistance are explained. A iron lithium complex oxide layer are formed at the outermost surface of the iron part by immersing the iron and steel parts in a salt bath containing cationic component of Li, Na and K and anionic components of CNO−and CO32−, where hydroxide compound selected from lithium hydroxide, sodium hydroxide and potassium hydroxide are added to the salt bath. Materials being in a hydrated state or in a free water containing state can be used for preparation or replenishing of the salt bath. An moistend air of (1×10−2 kg·H2O)/(1 kg dry air) can be used for mixing the salt bath. Containing ratio of Li, Na, K is preferable where a solidifying temperature of the mixture of carbonates of Li, Na, K in that ratio is lower than 500° C.

Abstract: An organopolysiloxane composition comprising (A) an organopolysiloxane, (B) a silane compound having at least two hydrolyzable groups or a partial hydrolyzate thereof, and (C) an antibacterial agent based on a ferrous compound, typically FeSO4 is antibacterial, mildew resistant, resistant to heat, resistant to weather, and safe.

Abstract: An antibacterial and mildewproofing organopolysiloxane composition comprising (A) an organopolysiloxane such as polydimethylsiloxane terminated with silanol groups or polydimethylsiloxane terminated with trimethylsiloxyl groups, (B) a hydrolyzable silane compound and/or a partial hydrolysis-condensation product thereof, (C) a triazolyl-group-containing compound such as tebuconazole and (D) an inorganic antibacterial agent comprising an inorganic substance comprising zeolite, apatite and/or silica and supporting or containing silver and/or silver ions.This composition is superior in antibacterial properties, mildew resistance and permanence of mildew resistance and also superior in weatherability such as heat resistance and ultraviolet light resistance, may cause less change in color, and is useful as a sealing medium.

Abstract: A mildew resistant organopolysiloxane composition is provided, including (A) an organopolysiloxane having silanol groups or alkoxyl groups, (B) a hydrolyzable silane, and (C) a triazolyl group-containing compound. The composition further includes (D) bis(2-pyridylthio-1-oxide) zinc salt. The composition is excellent in mildew resistance and its durability as well as excellent in heat resistance and weathering properties. The cured products hardly undergo discoloration if exposed to UV light or heat. The composition is useful as a sealant to be used at wet locations.

Abstract: A room temperature curable mildew resistant organopolysiloxane composition comprises (A) a hydroxyl or hydrolyzable group-containing organopolysiloxane, (B) a hydrolyzable organosilane such as methyltrimethoxysilane, methyltris(methylethylketoxime silane) or vinyltris(methylethylketoxime silane), a partially hydrolyzed product thereof or a mixture of the hydrolyzable organosilane with the partially hydrolyzed product thereof; and (C) a triazolyl group-containing compound such as 2-(4-chlorophenyl)ethyl-.alpha.-(1,1-dimethylethyl)-1H-1,2,4-triazole-1-yl -ethanol. Preferably, the component (B) does not contain aliphatic unsaturation in the molecule, and in this case, the component (B) free of aliphatic unsaturation is used in combination with (B') a hydrolyzable silane such as tetrakis(dimethylketoxime)silane, a partially hydrolyzed product thereof or a mixture of the hydrolyzable silane and the partially hydrolyzed product thereof.

Abstract: In a filter unit (25) and apparatus for desludging salt baths (1), which is flooded at least partially by the salt bath and is in working association with the upper end of a riser tube (23), the bath fluid to be desludged being driven, by means of a compressed air stream, for example, through the riser tube (23) toward the filter unit (9, 25), the filter cloth packet is made of woven wire of a nonferrous metal, preferably an alloy based on aluminum, nickel or titanium, and is surrounded by a filter frame (14), the frame (14) being shaped into a shallow, pyramidal frustum-shaped funnel (18) pointing toward the bottom of the vat, its apical bottom end being provided with a closable opening (19).