Abstract: Ceramic plates for side dams of twin-drum continuous strip casters comprising a REAG phase of 10 to 90 vol. %, a Sialon phase of 5 to 50 vol. %, a BN phase of 5 to 50 vol. % and an amorphous phase of over 0 to 20 vol. %, with the REAG phase comprising at least one rare-earth aluminum garnet phase selected from YAG, ErAG, YbAG and DyAG phases and the Sialon phase having a chemical formula, Si6?zAlzOzN8?z, wherein Z is between 0.05 and 1.9.

Abstract: Ceramic plates for side dams of twin-drum continuous strip casters comprising a REAG phase of 10 to 90 vol. %, a Sialon phase of 5 to 50 vol. %, a BN phase of 5 to 50 vol. % and an amorphous phase of over 0 to 20 vol. %, with the REAG phase comprising at least one rare-earth aluminum garnet phase selected from YAG, ErAG, YbAG and DyAG phases and the Sialon phase having a chemical formula, Si6-zAlzOzN8-z, wherein Z is between 0.05 and 1.9.

Abstract: The present invention relates to a ceramic plate material for side dams of a twin-drum strip caster, the ceramic plate material containing Al of 9 mass % or more in terms of Al equivalent and having the properties of; bending strength at room temperature of not less than 120 MPa, bending strength at 1,000° C. of not less than 65 MPa, hardness (Hv) of 50 to 350, fracture toughness KIC at 1,000° C. of not less than 1 MPa·m1/2, thermal conductivity in the temperature range from room temperature to 1,000° C. of not more than 8 W/(m·K), thermal shock resistance index R? of not less than 800 W/m, and wettability with molten steel (contact angle ?) of not less than 120°: and allows molten stainless steel to be continuously cast for a long period of time.

Abstract: The present invention relates to a ceramic plate material for side dams of a twin-drum strip caster, the ceramic plate material containing Al of 9 mass % or more in terms of Al equivalent and having the properties of; bending strength at room temperature of not less than 120 MPa, bending strength at 1,000° C. of not less than 65 MPa, hardness (Hv) of 50 to 350, fracture toughness KIC at 1,000° C. of not less than 1 MPa·m1/2, thermal conductivity in the temperature range from room temperature to 1,000° C. of not more than 8 W/(m·K), thermal shock resistance index R′ of not less than 800 W/m, and wettability with molten steel (contact angle &thgr;) of not less than 120°: and allows molten stainless steel to be continuously cast for a long period of time.

Abstract: While an insufficient lubricating effect caused by lack of lubricant is prevented and also while contamination of molten metal and insertion of molten metal caused by excessive feed of lubricant are prevented, a lubricating effect can be provided and continuous casting can be conducted over a long period of time. Molten metal is poured into a molten metal pool formed by a pair of cooling drums and side dams. The thus poured molten metal is cooled and solidified on circumferential surfaces of the cooling drums, so that a strip can be produced. In the above continuous strip casting method, the side dam is composed in such a manner that a portion of the ceramic plate on the inlet side in the rotational direction of the cooling drum is chamfered, wherein the portion comes into contact with an end surface of the cooling drum.