Abstract: To provide a method of melt-molding a vinylidene fluoride resin, in which the melt molding can be performed at a lower temperature. A composition is melt-molded at a shear rate of 1 s?1 to 600 s?1, where the composition contains a vinylidene fluoride resin having a weight average molecular weight of 250,000 to 450,000 and polyethylene having a melt flow rate of 0.04 g/10 min to 40 g/10 min, and an amount of the polyethylene being from 0.1 parts by mass to 5.0 parts by mass per 100 parts by mass of the vinylidene fluoride resin.

Abstract: A polyvinylidene fluoride resin composition containing a polyvinylidene fluoride resin and titanium oxide, wherein the content of the titanium oxide is 5 to 100 parts by weight per 100 parts by weight of the polyvinylidene fluoride resin, the resin composition contains, as a heat stabilizer, at least one compound selected from the group consisting of calcium polyhydroxymonocarboxylates, calcium salts of aliphatic carboxylic acids having 5 to 30 carbon atoms, calcium carbonate, calcium hydroxide, zinc oxide and magnesium oxide in a proportion of 0.1 to 20 parts by weight, and a weight ratio of the titanium oxide to the heat stabilizer is 100:1 to 3:1.

Abstract: A polyvinylidene fluoride resin composition containing a polyvinylidene fluoride resin and titanium oxide, wherein the content of the titanium oxide is 5 to 100 parts by weight per 100 parts by weight of the polyvinylidene fluoride resin, the resin composition contains, as a heat stabilizer, at least one compound selected from the group consisting of calcium polyhydroxymonocarboxylates, calcium salts of aliphatic carboxylic acids having 5 to 30 carbon atoms, calcium carbonate, calcium hydroxide, zinc oxide and magnesium oxide in a proportion of 0.1 to 20 parts by weight, and a weight ratio of the titanium oxide to the heat stabilizer is 100:1 to 3:1.