Abstract: In a manufacturing method for a sliding member, a nitrogen diffusion layer, a nitrogen compound layer, and an oxidation layer are formed by executing a first step of cooling a workpiece formed of a steel material after heating the workpiece in an atmosphere containing ammonia at 570 to 660° C., a second step of performing, subsequently to the first step, tempering while pressurizing a front surface side of the workpiece, and a third step of performing, subsequently to the second step, steam treatment of heating the workpiece in a steam atmosphere.

Abstract: In a manufacturing method for a sliding member, a nitrogen diffusion layer, a nitrogen compound layer, and an oxidation layer are formed by executing a first step of cooling a workpiece formed of a steel material after heating the workpiece in an atmosphere containing ammonia at 570 to 660° C., a second step of performing, subsequently to the first step, tempering while pressurizing a front surface side of the workpiece, and a third step of performing, subsequently to the second step, steam treatment of heating the workpiece in a steam atmosphere.

Abstract: A sliding member includes a base material portion formed of steel; a nitrogen diffusion layer with a thickness of 10 ?m to 50 ?m; and a nitrogen compound layer with a thickness of 10 ?m to 50 ?m. The nitrogen compound layer and the nitrogen diffusion layer are formed by performing a first heating process of performing heat treatment on a material formed of steel in an ammonia atmosphere at a temperature of 570° C. to 660° C., a second heating process of performing heat treatment on the material in a non-oxidizing and non-ammonia atmosphere at a temperature of 660° C. to 690° C., the temperature in the second heating process being higher than the temperature in the first heating process, and an oil cooling process of performing oil cooling treatment at an oil temperature of 60° C. to 80° C. subsequently to the second heating process.