Abstract: A homogeneous alumina-based sintered material having excellent grindability, low porosity and high flexural strength, and which is free of color unevenness and fluctuations in density. Predetermined amounts of Al.sub.2 O.sub.3 powder, MgO powder, CaCO.sub.3 powder and SiO.sub.2 powder are measured out, and then mixed with stirring in a ball mill. The mixture is granulated using a spray dryer, and then hydrostatically pressed to obtain a molded product having a predetermined shape. Subsequently, the molded product is stored and sintered at a temperature of 1,550.degree. C. to 1,650.degree. C., particularly 1,600.degree. C. to 1,650.degree. C. under atmospheric pressure for 2 hours. As a result, an alumina-based sintered material having a 50 percent cumulative grain size distribution in diameter of from 4 to 15 .mu.m, a 90 percent grain diameter of two to three times the 50 percent grain diameter, and a porosity of not more than 5% can be obtained.

Abstract: Disclosed is an alumina-based sintered material comprising a magnesium component, a calcium component, a silicon component, and a lithium component, wherein the content of the lithium component in terms of oxide amount is from 0.002 to 0.04% by weight based on the alumina-based sintered material.

Abstract: A silicon nitride sintered product and processes for the production thereof are described, wherein the product comprises from 75 to 97.9% by weight of silicon nitride, from 2 to 20% by weight of yttrium oxide and cerium oxide in a molar ratio of cerium oxide to yttrium oxide of 0.4/1 to 4/1, and from 0.1 to 8% by weight of aluminum oxide.

Abstract: A process for producing a silicon nitride sintered product having high toughness is described, comprising blending from 97 to 57% by weight of metallic silicon powder having a maximum particle size of 25 .mu.m or less with from 1 to 15% by weight, calculated as TiN, of a TiN powder having a maximum particle size of 20 .mu.m or less or a powder of titanium component capable of changing into TiN during reaction sintering, and from 2 to 28% by weight of one or more components selected from the group consisting of AlN, Al.sub.2 O.sub.3, SiO.sub.2 and oxides of rare earth elements, molding the resulting mixture, carrying out reaction sintering in a nonoxidizing atmosphere of a nitrogen gas or a nitrogen-containing mixed gas, and thereafter resintering in the same atmosphere at a temperature of from 1,600.degree. C. to 2,200.degree. C.