Abstract: The electrically conductive resin composition may contain matrix resin, coke powder, and carbon fiber. The volume mean particle diameter of the coke powder may be not less than 1 ?m and not more than 500 ?m. The content percentage of the coke powder in the electrically conductive resin composition may be not less than 1 wt % and not more than 60 wt %. The aspect ratio of the carbon fiber may be not less than 3 and not more than 1700. The content percentage of the carbon fiber in the electrically conductive resin composition may be not less than 0.5 wt % and not more than 10 wt %.

Abstract: Provided is carbon material filler for an electromagnetic shield, which includes a graphitizable carbon material to be mixed into a molding material in order to absorb electromagnetic waves, the carbon material filler for an electromagnetic shield satisfying (1) to (3): (1) A spacing d002 of a 002 plane of the graphitizable carbon material measured through X-ray diffraction measurement (XRD) is at least 0.338 nm. (2) A relative intensity ratio (A/B) value between a peak intensity (A) of a “002 plane” detected when the graphitizable carbon material is measured through X-ray diffraction measurement (XRD) and a higher peak intensity (B) that is selected from a “100 plane” and a “004 plane” is at least 2.5 and less than 27. (3) The filler is in powder form and the average particle diameter D50 is at least 1 ?m and at most 5 mm.

Abstract: The electrically conductive resin composition may contain matrix resin, coke powder, and carbon fiber. The volume mean particle diameter of the coke powder may be not less than 1 ?m and not more than 500 ?m. The content percentage of the coke powder in the electrically conductive resin composition may be not less than 1 wt % and not more than 60 wt %. The aspect ratio of the carbon fiber may be not less than 3 and not more than 1700. The content percentage of the carbon fiber in the electrically conductive resin composition may be not less than 0.5 wt % and not more than 10 wt %.

Abstract: Provided is carbon material filler for an electromagnetic shield, which includes a graphitizable carbon material to be mixed into a molding material in order to absorb electromagnetic waves, the carbon material filler for an electromagnetic shield satisfying (1) to (3): (1) A spacing d002 of a 002 plane of the graphitizable carbon material measured through X-ray diffraction measurement (XRD) is at least 0.338 nm. (2) A relative intensity ratio (A/B) value between a peak intensity (A) of a “002 plane” detected when the graphitizable carbon material is measured through X-ray diffraction measurement (XRD) and a higher peak intensity (B) that is selected from a “100 plane” and a “004 plane” is at least 2.5 and less than 27. (3) The filler is in powder form and the average particle diameter D50 is at least 1 ?m and at most 5 mm.