Abstract: The present invention provides a polyvinyl chloride-based resin molded product obtained by molding a resin mixture containing 1 to 50 parts by weight of calcium carbonate having an average primary particle size of 0.01 to 0.3 ?m and 5 to 18 parts by weight of an impact modifier per 100 parts by weight of a polyvinyl chloride-based resin, wherein a Charpy impact strength at 0° C. is 20 kJ/m2 or more, and a Vicat softening temperature is 85° C. or higher, and a method for manufacturing the polyvinyl chloride-based resin molded product.

Abstract: The present invention provides a polyvinyl chloride-based rigid molded product containing 10 to 40 parts by weight of calcium carbonate having an average primary particle size of 0.01 to 0.3 ?m per 100 parts by weight of a polyvinyl chloride-based resin having an average polymerization degree of 500 to 1,500, wherein a variation coefficient of the number of calcium carbonate particles in partitioning analysis of a cross section of the molded product is 15% or less, and a method for manufacturing the same.

Abstract: The present invention provides a polyvinyl chloride-based resin molded product obtained by molding a resin mixture containing 3 to 15 parts by weight of calcium carbonate having an average primary particle size of 0.01 to 0.3 ?m and 2 to 4 parts by weight of an impact modifier per 100 parts by weight of a polyvinyl chloride-based resin, wherein a Charpy impact strength at 23° C. is 20 kJ/m2 or more, and a weight reduction ratio is 1.5 mg/cm2 or less when the molded product is immersed in a 93% by weight sulfuric acid aqueous solution for 14 days in accordance with JIS K 6745, and a method for manufacturing the polyvinyl chloride-based resin molded product.

Abstract: The present invention provides a polyvinyl chloride-based resin molded product obtained by molding a resin mixture containing 3 to 15 parts by weight of calcium carbonate having an average primary particle size of 0.01 to 0.3 ?m and 2 to 4 parts by weight of an impact modifier per 100 parts by weight of a polyvinyl chloride-based resin, wherein a Charpy impact strength at 23° C. is 20 kJ/m2 or more, and a weight reduction ratio is 1.5 mg/cm2 or less when the molded product is immersed in a 93% by weight sulfuric acid aqueous solution for 14 days in accordance with JIS K 6745, and a method for manufacturing the polyvinyl chloride-based resin molded product.

Abstract: The present invention provides a polyvinyl chloride-based resin molded product obtained by molding a resin mixture containing 1 to 50 parts by weight of calcium carbonate having an average primary particle size of 0.01 to 0.3 ?m and 5 to 18 parts by weight of an impact modifier per 100 parts by weight of a polyvinyl chloride-based resin, wherein a Charpy impact strength at 0° C. is 20 kJ/m2 or more, and a Vicat softening temperature is 85° C. or higher, and a method for manufacturing the polyvinyl chloride-based resin molded product.

Abstract: The present invention provides a polyvinyl chloride-based rigid molded product containing 10 to 40 parts by weight of calcium carbonate having an average primary particle size of 0.01 to 0.3 ?m per 100 parts by weight of a polyvinyl chloride-based resin having an average polymerization degree of 500 to 1,500, wherein a variation coefficient of the number of calcium carbonate particles in partitioning analysis of a cross section of the molded product is 15% or less, and a method for manufacturing the same.