Abstract: Rolled steel bar for hot forging consisting, by mass percent, of C: 0.25-0.50%, Si: 0.40-1.0%, Mn: 1.0-1.6%, S: 0.005-0.035%, Al: 0.005-0.050%, V: 0.10-0.30%, N: 0.005-0.030% with the balance being Fe and impurities, i.e., P: 0.035% or less and O: 0.0030% or less, wherein Fn1=C+Si/10+Mn/5+5Cr/22+1.65V?5S/7 is 0.90 to 1.20. The predicted maximum width of nonmetallic inclusions at the time when a cumulative distribution function obtained by extreme value statistical processing by taking the width of nonmetallic inclusion in an R1/2 part of a longitudinal cross section of the steel bar as W (mm) is 99.99% is 100 ?m or narrower. The number density of sulfides each having a circle-equivalent diameter of 0.3 to 1.0 ?m observed per unit area of the R1/2 part of a transverse cross section of the steel bar is 500 pieces/mm2 or higher.

Abstract: A rolled steel bar for hot forging consisting, by mass percent, of C: 0.25-0.50%, Si: 0.40-1.0%, Mn: 1.0-1.6%, S: 0.005-0.035%, Al: 0.005-0.050%, V: 0.10-0.30%, and N: 0.005-0.030%, and the balance of Fe and impurities, i.e., P: 0.035% or less and O: 0.0030% or less, wherein Fn1=C+Si/10+Mn/5+5Cr/22+1.65V?5S/7 is 0.90 to 1.20. The predicted maximum width of nonmetallic inclusions at the time when a cumulative distribution function obtained by extreme value statistical processing by taking the width of nonmetallic inclusion in an R1/2 part of a longitudinal cross section of the steel bar as W (?m) is 99.99% is 100 ?m or narrower. The number density of sulfides each having a circle-equivalent diameter of 0.3 to 1.0 ?m observed per unit area of the R1/2 part of a transverse cross section of the steel bar is 500 pieces/mm2 or higher.

Abstract: A rolled steel bar for hot forging consisting, by mass percent, of C: 0.25-0.50%, Si: 0.40-1.0%, Mn: 1.0-1.6%, S: 0.005-0.035%, Al: 0.005-0.050%, V: 0.10-0.30%, and N: 0.005-0.030%, and the balance of Fe and impurities, i.e., P: 0.035% or less and O: 0.0030% or less, wherein Fn1=C+Si/10+Mn/5+5Cr/22+1.65V?5S/7 is 0.90 to 1.20. The predicted maximum width of nonmetallic inclusions at the time when a cumulative distribution function obtained by extreme value statistical processing by taking the width of nonmetallic inclusion in an R1/2 part of a longitudinal cross section of the steel bar as W (mm) is 99.99% is 100 mm or narrower. The number density of sulfides each having a circle-equivalent diameter of 0.3 to 1.0 mm observed per unit area of the R1/2 part of a transverse cross section of the steel bar is 500 pieces/mm2 or higher.

Abstract: A rolled steel bar for hot forging consisting, by mass percent, of C: 0.25-0.50%, Si: 0.40-1.0%, Mn: 1.0-1.6%, S: 0.005-0.035%, Al: 0.005-0.050%, V: 0.10-0.30%, and N: 0.005-0.030%, and the balance of Fe and impurities, i.e., P: 0.035% or less and O: 0.0030% or less, wherein Fn1=C+Si/10+Mn/5+5Cr/22+1.65V?5S/7 is 0.90 to 1.20. The predicted maximum width of nonmetallic inclusions at the time when a cumulative distribution function obtained by extreme value statistical processing by taking the width of nonmetallic inclusion in an R1/2 part of a longitudinal cross section of the steel bar as W (mm) is 99.99% is 100 mm or narrower. The number density of sulfides each having a circle-equivalent diameter of 0.3 to 1.0 mm observed per unit area of the R1/2 part of a transverse cross section of the steel bar is 500 pieces/mm2 or higher.