Abstract: The amorphous silica has a large apparent specific gravity despite of its BET specific surface area of 200 to 500 m.sup.2 /g, has an oil absorption amount of as small as 50 to 120 ml/100 g, has an agglomeration degree (D1/D0=DA) defined by the ratio of silica elementary particle diameter D0 to primary particle diameter D1 of from 10 to 50, and has nearly a spherical particulate structure which is quite different from that of the conventional gelation method silica (DA=OO). The amorphous silica-type filler exhibits excellent properties in regard to handling, processability, dispersion property and abrasion-resistant property and, when added as, for example, an anti-blocking agent, makes it possible to obtain resin films having transparency and scratch-resistant property without fisheyes or voids.

Abstract: The amorphous silica has a large apparent specific gravity despite of its BET specific surface area of 200 to 500 m.sup.2 /g, has an oil-absorption amount of as small as 50 to 120 ml/100 g, has an agglomeration degree (D1/D0=DA) defined by the ratio of silica elementary particle diameter D0 to primary particle diameter D1 of from 10 to 50, and has nearly a spherical particulate structure which is quite different from that of the conventional gelation method silica (DA=.infin.). The amorphous silica-type filler exhibits excellent properties in regard to handling, processability, dispersion property and abrasion-resistant property and, when added as, for example, an anti-blocking agent, makes it possible to obtain resin films having transparency and scratch-resistant property without fisheyes or voids.

Abstract: The amorphous silica has a large apparent specific gravity despite of its BET specific surface area of 20 to 500 m.sup.2 /g, has an oil absorption amount of as small as 50 to 120 ml/100 g, has an agglomeration degree (D1/D0=DA) defined by the ratio of silica elementary particle diameter D0 to primary particle diameter D1 of from 10 to 50, and has nearly a spherical particulate structure which is quite different from that of the conventional gelation method silica (DA=.infin.). The amorphous silica-type filler exhibits excellent properties in regard to handling, processability, dispersion property and abrasion-resistant property and, when added as, for example, an anti-blocking agent, makes it possible to obtain resin films having transparency and scratch-resistant property without fisheyes or voids.

Abstract: Disclosed is a filler for ink jet recording paper, said filler being composed of amorphous silica having a median diameter, measured by the coulter counter method, of 2 to 15 .mu.m, an oil absorption of at least 180 ml/100 g, a refractive index, measured by the solvent method, of at least 1.450, and a moisture absorption, measured when it is caused to absorb moisture for 200 hours at a relative humidity of 90% and a temperature of 25.degree. C., of at least 35%.

Abstract: Disclosed is a filler for ink jet recording paper, said filler being composed of amorphous silica having a median diameter, measured by the coulter counter method, of 2 to 15 .mu.m, an oil absorption of at least 180 ml/100 g, a refractive index, measured by the solvent method, of at least 1.450, and a moisture absorption, measured when it is caused to absorb moisture for 200 hours at a relative humidity of 90% and a temperature of 25.degree. C., of at least 35%.