Abstract: An object of the present invention is to provide a catalyst that enables production of an unsaturated carboxylic acid and/or unsaturated carboxylic acid ester represented by methyl methacrylate with high selectivity. The object is achieved by a catalyst including: one or more elements selected from boron, magnesium, zirconium, hafnium, and titanium; one or more elements selected from alkali metal elements; and silica; the catalyst having a peak height ratio I2/I1 of 0 to 1.2, wherein I1 represents the peak height at 417±10 cm?1, and I2 represents the peak height at 1050±10 cm?1, as obtained by Raman spectroscopy.

Abstract: A surface modified quartz glass crucible and a process for modifying the crucible includes a layer of a metal oxide on the whole or a part of the inside and/or outside of the crucible, and baking it. At least an inside surface of the crucible is coated with a said metal oxide of magnesium, calcium, strontium or barium. The coated layer of the crucible does not abrade easily and provides a high dislocation free ratio of silicon single crystals pulled by using the crucible.

Abstract: A silica glass crucible used for pulling up silicon single crystal at a high temperature. The silica glass crucible may have at least an outer surface of a wall part of the crucible covered with fine grooves having a length of less than 200 ?m, a width of less than 30 ?m and a depth of from more than 3 ?m to less than 30 ?m. The fine groves may be formed by carrying out a sand-blast treatment and a hydrofluoric acid etching and may exist on more than 10% of the outer surface of the crucible, and a sliding frictional coefficient of the outer surface of the crucible to a carbon at 1500° C. is more than 0.6.

Abstract: A surface modified quartz glass crucible and a process for modifying the crucible includes a layer of a metal oxide on the whole or a part of the inside and/or outside of the crucible, and baking it. At least an inside surface of the crucible is coated with a said metal oxide of magnesium, calcium, strontium or barium. The coated layer of the crucible does not abrade easily and provides a high dislocation free ratio of silicon single crystals pulled by using the crucible.

Abstract: A process reinforcing a silica glass substance, such as a silica glass crucible, is provided without intermixing an impurity. The process comprises forming a silica glass powder layer on a surface of the silica glass substance, and crystallizing said silica glass powder layer under high temperature. As for a silica glass crucible, the process for reinforcing the silica glass crucible and the reinforced silica glass crucible are provided, wherein the silica glass powder layer on the whole or a part of the surface of the crucible is formed and then, crystallized under a temperature at the melting of a silicon raw material being charged into said quartz glass crucible.

Abstract: To provide a silica glass crucible, wherein there are no problems of generating a sinking and buckling when said crucible is used for pulling up silicon single crystal at a high temperature. The silica glass crucible used for pulling up the silicon single crystal, wherein at least an outer surface of a wall part of the crucible is covered with fine grooves having a length of less than 200 ?m, a width of less than 30 ?m and a depth of from more than 3 ?m to less than 30 ?m. Preferably, said fine groves are formed by carrying out a sand-blast treatment and a hydrofluoric acid etching and exist on more than 10% of the outer surface of the crucible, and a sliding frictional coefficient of the outer surface of the crucible to a carbon at 1500 degree C. is more than 0.6.

Abstract: A surface modified quartz glass crucible and a process for modifying the crucible includes a layer of a metal oxide on the whole or a part of the inside and/or outside of the crucible, and baking it. At least an inside surface of the crucible is coated with a said metal oxide of magnesium, calcium, strontium or barium. The coated layer of the crucible does not abrade easily and provides a high dislocation free ratio of silicon single crystals pulled by using the crucible.

Abstract: To provide a silica glass crucible, wherein there are no problems of generating a sinking and buckling when said crucible is used for pulling up silicon single crystal at a high temperature. The silica glass crucible used for pulling up the silicon single crystal, wherein at least an outer surface of a wall part of the crucible is covered with fine grooves having a length of less than 200 ?m, a width of less than 30 ?m and a depth of from more than 3 ?m to less than 30 ?m. Preferably, said fine groves are formed by carrying out a sand-blast treatment and a hydrofluoric acid etching and exist on more than 10% of the outer surface of the crucible, and a sliding frictional coefficient of the outer surface of the crucible to a carbon at 1500 degree C. is more than 0.6.

Abstract: A process reinforcing a silica glass substance, such as a silica glass crucible, is provided without intermixing an impurity. The process comprises forming a silica glass powder layer on a surface of the silica glass substance, and crystallizing said silica glass powder layer under high temperature. As for a silica glass crucible, the process for reinforcing the silica glass crucible and the reinforced silica glass crucible are provided, wherein the silica glass powder layer on the whole or a part of the surface of the crucible is formed and then, crystallized under a temperature at the melting of a silicon raw material being charged into said quartz glass crucible.

Abstract: A surface modified quartz glass crucible and a process for modifying the crucible includes a layer of a metal oxide on the whole or a part of the inside and/or outside of the crucible, and baking it. At least an inside surface of the crucible is coated with a said metal oxide of magnesium, calcium, strontium or barium. The coated layer of the crucible does not abrade easily and provides a high dislocation free ratio of silicon single crystals pulled by using the crucible.

Abstract: To provide a silica glass crucible, wherein there are no problems of generating a sinking and buckling when said crucible is used for pulling up silicon single crystal at a high temperature. The silica glass crucible used for pulling up the silicon single crystal, wherein at least an outer surface of a wall part of the crucible is covered with fine grooves having a length of less than 200 &mgr;m, a width of less than 30 &mgr;m and a depth of from more than 3 &mgr;m to less than 30 &mgr;m. Preferably, said fine groves are formed by carrying out a sand-blast treatment and a hydrofluoric acid etching and exist on more than 10% of the outer surface of the crucible, and a sliding frictional coefficient of the outer surface of the crucible to a carbon at 1500 degree C. is more than 0.6.

Abstract: A process reinforcing a silica glass substance, such as a silica glass crucible, is provided without intermixing an impurity. The process comprises forming a silica glass powder layer on a surface of the silica glass substance, and crystallizing said silica glass powder layer under high temperature. As for a silica glass crucible, the process for reinforcing the silica glass crucible and the reinforced silica glass crucible are provided, wherein the silica glass powder layer on the whole or a part of the surface of the crucible is formed and then, crystallized under a temperature at the melting of a silicon raw material being charged into said quartz glass crucible.

Abstract: A process for modifying the surface of a quartz glass crucible and a modified quartz glass crucible produced by the process, where the crucible has a transparent coated layer containing a crystallization accelerator on the surface. The process includes coating a mixed solution containing a metal salt and a partial hydrolyzate of alkoxysilane oligomer on the surface of the crucible and heating to obtain a quartz glass crucible having a transparent coated layer. The crystallization accelerator contains a metal oxide or a metal carbonate dispersed in a silica matrix.

Abstract: A process for modifying the surface of a quartz glass crucible and a modified quartz glass crucible produced by the process, where the crucible has a transparent coated layer containing a crystallization accelerator on the surface. The process includes coating a mixed solution containing a metal salt and a partial hydrolyzate of alkoxysilane oligomer on the surface of the crucible and heating to obtain a quartz glass crucible having a transparent coated layer. The crystallization promoter contains a metal oxide or a metal carbonate dispersed in a silica matrix.

Abstract: A surface modified quartz glass crucible and a process for modifying the crucible includes a layer of a metal oxide on the whole or a part of the inside and/or outside of the crucible, and baking it. At least an inside surface of the crucible is coated with a said metal oxide of magnesium, calcium, strontium or barium. The coated layer of the crucible does not abrade easily and provides a high dislocation free ratio of silicon single crystals pulled by using the crucible.

Abstract: A process for modifying the surface of a quartz glass crucible and a modified quartz glass crucible produced by the process, where the crucible has a transparent coated layer containing a crystallization accelerator on the surface. The process includes coating a mixed solution containing a metal salt and a partial hydrolyzate of alkoxysilane oligomer on the surface of the crucible and heating to obtain a quartz glass crucible having a transparent coated layer. The crystallization accelerator contains a metal oxide or a metal carbonate dispersed in a silica matrix.