Abstract: A method for desulfurizing molten steel comprising taking a sample out from molten steel after tapping from a converter or during secondary refining and analyzing the sample rapidly with high accuracy by a method comprising a high frequency induction heating step wherein the sample is combusted and oxidized under the high frequency induction heating in an oxygen atmosphere having an oxygen purity of 99.5 vol % or more to convert S in the sample into SO2 and an analyzing step wherein SO2-containing gas produced in the high frequency induction heating step is analyzed through an ultraviolet fluorescence method to quantify S concentration of the sample.

Abstract: A method for desulfurizing molten steel comprising taking a sample out from molten steel after tapping from a converter or during secondary refining and analyzing the sample rapidly with high accuracy by a method comprising a high frequency induction heating step wherein the sample is combusted and oxidized under the high frequency induction heating in an oxygen atmosphere having an oxygen purity of 99.5 vol % or more to convert S in the sample into SO2 and an analyzing step wherein SO2-containing gas produced in the high frequency induction heating step is analyzed through an ultraviolet fluorescence method to quantify S concentration of the sample.

Abstract: A method for desulfurizing molten steel comprising taking a sample out from molten steel after tapping from a converter or during secondary refining and analyzing the sample rapidly with high accuracy by a method comprising a high frequency induction heating step wherein the sample is combusted and oxidized under the high frequency induction heating in an oxygen atmosphere having an oxygen purity of 99.5 vol % or more to convert S in the sample into SO2 and an analyzing step wherein SO2-containing gas produced in the high frequency induction heating step is analyzed through an ultraviolet fluorescence method to quantify S concentration of the sample.

Abstract: There are provided a method for desulfurizing molten steel, characterized in that a sample taken out from molten steel after the tapping from a converter or during the secondary refining is analyzed rapidly in a high accuracy by a method comprising a high frequency induction heating step wherein the sample is combusted and oxidized under the high frequency induction heating in a pure oxygen atmosphere to convert S in the sample into SO2 and an analyzing step wherein SO2-containing gas produced in the high frequency induction heating step is analyzed through an ultraviolet fluorescence method to quantify S concentration of the sample, whereby S concentration of molten steel after the tapping from the converter can be controlled in a high accuracy to prevent failure of S concentration and also desulfurization time in the secondary refining can be shortened and the amount of the desulfurizer or the like used can be reduced, and a method of manufacturing molten steel by using such a method.