Abstract: A method for producing a rubber composition containing by weight 5 to 95 parts of natural rubber (NR), 95 to 5 parts of chloroprene rubber (CR), and 20 to 90 parts of carbon black (CB), using a kneading machine, includes a first step of producing a master batch (M1) containing NR and CB; a second step of producing a master batch (M2) containing CR and CB, and a third step of mixing the M1 and M2 with each other to produce a master batch (M3) containing NR, CR, and CB, wherein the amount of CB contained in the M2 is from 40 to 70% by weight relative to the total amount of CB in the rubber composition, and when the M2 is discharged from the kneading machine after the second step, the actually measured temperature of the rubber composition is from 100 to 130° C.

Abstract: A method for producing a rubber composition containing by weight 5 to 95 parts of natural rubber (NR), 95 to 5 parts of chloroprene rubber (CR), and 20 to 90 parts of carbon black (CB), using a kneading machine, includes a first step of producing a master batch (M1) containing NR and CB; a second step of producing a master batch (M2) containing CR and CB, and a third step of mixing the M1 and M2 with each other to produce a master batch (M3) containing NR, CR, and CB, wherein the amount of CB contained in the M2 is from 40 to 70% by weight relative to the total amount of CB in the rubber composition, and when the M2 is discharged from the kneading machine after the second step, the actually measured temperature of the rubber composition is from 100 to 130° C.

Abstract: A method of producing a rubber-resin composite whose vulcanized rubber and thermoplastic resin moldings are bonded together by high adhesive strength at low cost, satisfying both moldability and mechanical strength. It comprises: (1) making the vulcanized rubber molding by vulcanization molding, (2) forming an adhesive layer, whose principal ingredient is chlorosulfonated polyethylene, on a surface of the rubber molding to be bonded to the resin, and (3) while arranging the rubber molding in a mold, pouring the thermoplastic resin containing 30˜60 wt. % of glass fiber in a molten state into the mold to form the resin molding.

Abstract: A method of producing a rubber-resin composite whose vulcanized rubber and thermoplastic resin moldings are bonded together by high adhesive strength at low cost, satisfying both moldability and mechanical strength. It comprises: (1) making the vulcanized rubber molding by vulcanization molding, (2) forming an adhesive layer, whose principal ingredient is chlorosulfonated polyethylene, on a surface of the rubber molding to be bonded to the resin, and (3) while arranging the rubber molding in a mold, pouring the thermoplastic resin containing 30˜60 wt. % of glass fiber in a molten state into the mold to form the resin molding.

Abstract: The present invention provides a liquid-enclosing type vibration isolating device of all around stopper type with a reliable stopper action at a time of a large displacement of a main body metal fitting in the device, in a liquid-enclosing type vibration isolating device in which a main body metal fitting and a mounting metal fitting disposed thereunder are connected to each other through a vibration isolating body formed with a rubber elastic member with a liquid being sealed therewithin, the lower mounting metal fitting comprises a boss metal fitting integrally formed with a mounting bolt and inserted into the vibration isolating body, a spacer metal fitting having a flange portion for a stopper at the upper portion and fitted into the boss metal fitting, and a mounting plate metal fitting fixed to the boss metal fitting so as to hold the spacer metal fitting in a fixed state, a required clearance is provided between the flange portion of the spacer metal fitting and the plate metal fitting, and a lower end